SABIC Innovative Plastics LNP STAT-KON DX05305C PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON DX05305C PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-KON* DX05305C is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive, Clean Compounding System.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ASTM D792 |
| 1.22 g/cc | 0.0441 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0074 cm/cm @Time 86400 sec |
0.0074 in/in @Time 24.0 hour |
ISO 294 |
| Linear Mold Shrinkage, Transverse | 0.0061 cm/cm @Time 86400 sec |
0.0061 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 52.0 MPa | 7540 psi | ASTM D638 |
| 54.0 MPa | 7830 psi | ISO 527 | |
| Tensile Strength, Yield | 22.0 MPa | 3190 psi | ASTM D638 |
| Elongation at Break | 5.9 % | 5.9 % | ASTM D638 |
| Elongation at Yield | 1.9 % | 1.9 % | ASTM D638 |
| Tensile Modulus | 2.62 GPa | 380 ksi | 1 mm/min; ISO 527 |
| 2.65 GPa | 384 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 96.0 MPa | 13900 psi | ASTM D790 |
| 101 MPa | 14600 psi | ISO 178 | |
| Flexural Modulus | 2.59 GPa | 376 ksi | ASTM D790 |
| 2.73 GPa | 396 ksi | ISO 178 | |
| Izod Impact, Notched | 0.480 J/cm | 0.899 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 10.12 J/cm | 18.96 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 80.0 kJ/m² | 38.1 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 2.00 J | 1.48 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 5.00 J | 3.69 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 61.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
34.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 64.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
36.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 61.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
34.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 61.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
34.2 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 142 °C @Thickness 3.20 mm |
288 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 132 °C | 270 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 135 °C @Thickness 3.20 mm |
275 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 100 ohm-cm - 1e+05 | 100 ohm-cm - 1e+05 | ASTM D257 |
| Surface Resistance | 100 ohm - 1e+05 | 100 ohm - 1e+05 | ASTM D257 |
Users viewing this material also viewed the following:
- PolyOne Geon™ HC 2170G Polyvinyl Chloride, Flexible (PVC, Flexible)
- Polimeri Europa SINKRAL B813 ABS, Impact Grade (discontinued **)
- Global PC-1603 Standard Grade Polycarbonate
- Karina E 836-10/176-CRA White PVC Compound
- Unipetrol PE HD LITEN® MB/ML 67 HDPE
- Chosun Refractories A-2 Insulating Firebrick
- Brandenburger S 5000 Ablation Material for Aeronautics and Space Aviation
- Axiall 15880-02 Wire & Cable Flexible PVC
Copyright © lookpolymers.com All Rights Reserved