Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | <= 82.0 MPa | <= 11900 psi | ISO 178 |
Polykemi AB SCANBLEND FS7 UV4 PC/ASA Blend with Improved Weather Resistance Information provided by Polykemi AB |
|||
Flexural Strength | 82.0 MPa | 11900 psi | ASTM D790 |
PolyOne Geon™ Vinyl Dry Blend E6755 Polyvinyl Chloride, Rigid (PVC, Rigid) Information provided by PolyOne |
|||
Flexural Strength | 82.0 MPa | 11900 psi | ASTM D790 |
SABIC Innovative Plastics LNP FARADEX PS003E PA 6 (Europe-Africa-Middle East) LNP* Faradex* PS003E is a compound based on Nylon 6 resin containing Stainless Steel. Added features of this material include: Electrically Conductive, EMI/RFI Shielding. |
|||
Flexural Strength | 82.0 MPa | 11900 psi | 2mm/min; ASTM D790 |
Kingfa MAC-601 PC/ABS Alloy Features:Excellent balance propertiesHigh impact strengthGood electro-plating propertiesGood processing propertiesApplications:Injection moldingAutomobile instrument panelElectrical and electronic p.. |
|||
Flexural Strength | 82.0 MPa | 11900 psi | 2mm/min; ASTM D790 |
Kingfa PC-S609 Toughened PC Features:Good mechanical propertiesSuper high impact strengthGood weather resistanceHigh glossGood processing propertiesStress cracking propertiesApplications:OA and IT partsAutomobile accessoriesEl.. |
|||
Flexural Strength | 82.0 MPa | 11900 psi | ASTM D790 |
LG Chemical LUPOY HF-5000 High Flow PC/ABS Alloy, Unreinforced Among the characteristics of LUPOY polycarbonate resins are excellent mechanical properties, high heat resistance, high impact strength, and dimensional stability.Applications:Automotive: Automotive.. |
|||
Flexural Strength | 82.0 MPa | 11900 psi | 2mm/min; ASTM D790 |
Kingfa MAC-451 UV Modified PC/ABS Alloy Features:Excellent balance propertiesGood weather resistanceGood impact strengthGood processing propertiesSuit for electro-platingApplications:Injection moldingAutomobile license plateWater tank cov.. |
|||
Flexural Strength | 82.0 MPa | 11900 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP DL003E PC (Asia Pacific) LNP LUBRICOMP* DL003E is a compound based on Polycarbonate resin containing PTFE. Added features of this material include: Easy Molding. |
|||
Flexural Strength | 82.0 MPa | 11900 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
SABIC Innovative Plastics LNP Lubricomp DP0039 PC LNP* Lubricomp* DP0039 is a Polycarbonate base resin containing PTFE and Silicone lubricants. Characteristics are: Flame Retardant.This data was supplied by SABIC-IP for the Americas region. |
|||
Flexural Strength | 82.0 MPa | 11900 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP KFP032 Acetal Copolymer (Asia Pacific) LNP* LUBRICOMP* KFP032 is a compound based on Acetal Copolymer resin containing PTFE, Silicone, Glass Fiber. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 82.0 MPa | 11900 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP OP005XXC PPS - LINEAR LNP LUBRICOMP* OP005XXC is a compound based on PPS - Linear resin containing 25% PTFE/Silicone. Added features of this material include: Wear Resistant. |
|||
Flexural Strength | 82.0 MPa | 11900 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP OP005XXC PPS (Asia Pacific) LNP* LUBRICOMP* OP005XXC is a compound based on Polyphenylene Sulfide resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 82.0 MPa | 11900 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRILOY R2000 PA 66 LNP* LUBRILOY* R2000 is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added feature of this material is: Wear Resistant. |
|||
Flexural Strength | 82.0 MPa | 11900 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
SABIC Innovative Plastics Valox® 357M PBT (Asia Pacific) This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Flexural Strength | 82.0 MPa | 11900 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
SABIC Innovative Plastics Valox® 357U PBT Unreinforced PBTP, UL94 V-0/5VA rated. Improved UV resistant version of VALOX 357. Nonblooming flame retardant.This data was supplied by SABIC-IP for the Americas region. |
|||
Flexural Strength | 82.0 MPa | 11900 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP AX90213 ABS LNP* THERMOCOMP* AX90213 is a compound based on ABS resin containing Glass Fiber. |
|||
Flexural Strength | 82.0 MPa | 11900 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP AX90213 ABS (Asia Pacific) LNP* Thermocomp* AX90213 is a compound based on Acrylonitrile Butadiene Styrene resin containing Glass Fiber. |
|||
Flexural Strength | 82.0 MPa | 11900 psi | ASTM D 790 |
SABIC Innovative Plastics LNP Thermocomp MX88073 PP (Asia Pacific) LNP* Thermocomp* MX88073 is a compound based on Polypropylene resin containing Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Flexural Strength | 82.0 MPa | 11900 psi | ISO 178 |
SABIC Innovative Plastics LNP STAT-KON KD000 Acetal Copolymer LNP* STAT-KON* KD000 is a compound based on Acetal resin containing Proprietary Filler(s). Added feature of this material is: Electrically Conductive. |
|||
Flexural Strength | 82.0 MPa | 11900 psi | ASTM D790 |
SABIC Innovative Plastics LNP STAT-KON RD000I PA 66 (Asia Pacific) LNP* STAT-KON* RD000I is a compound based on Nylon 66 resin containing Carbon Powder, Impact Modifier. Added features of this material include: Electrically Conductive, High Impact. |
|||
Flexural Strength | 82.0 MPa | 11900 psi | ASTM D 790 |
SABIC Innovative Plastics LNP Thermocomp OF002A PPS LNP* Thermocomp* OF002A is a compound based on Polyphenylene Sulfide resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region. |
|||
Flexural Strength | 82.0 MPa | 11900 psi | ASTM D790 |
Unitika P-1001 Engineering Plastic P series resins are resins succeeding the characteristics of the neat polymer, U100, and improved in flowability and optical properties. Among many super engineering plastics, the resins are few tra.. |
|||
Flexural Strength | 82.0 MPa | 11900 psi | ISO 178 |
Polyplastics Duranex® 209A Polybutylene Terephthalate (PBT), Low friction, Low wear DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers .. |
|||
Flexural Strength | 82.0 MPa | 11900 psi | ASTM D790, ISO 178 |
EPICHEM PA 6 Polyamide 6 Characteristics: medium viscosity, general purpose |
|||
Flexural Strength | 82.0 MPa | 11900 psi | dry; ISO 178 |
Azoty Tarnow™ Tarnamid® T-30 Polyamide 6 - Natural High viscosity extrusion grade for blown and flat films, including biaxial oriented films, also for extrusion of rods, pipes, plates, sheets, low diameter tubes and for injection molding of thick-wa.. |
|||
Flexural Strength | 82.0 MPa | 11900 psi | 2.6 mm/min; ASTM D790 |
BLUESTAR LXS 312 PPE-HIPS, 20% Mineral Filled Typical Applications: LED shellInformation provided by Polymer Technology and Services, LLC (PTS). |
|||
Flexural Strength | 82.0 MPa | 11900 psi | dry; ISO 178 |
Azoty Tarnow™ Tarnamid® T-30 MS Polyamide 6 - Natural High viscosity extrusion grade for blown and flat films, including biaxial oriented films, also for extrusion of rods, pipes, plates, sheets, low diameter tubes and for injection molding of thick-wa.. |
|||
Flexural Strength | 82.0 MPa | 11900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics NORYL RN0712 PPE+HIPS (Europe-Africa-Middle East) Noryl RN0712 is an unfilled Post Consumer recycle (PCR) based injection moldable modified polyphenylene ether resin comprising at least 37% PCR styrenic series resin content. Designed for good dimen.. |
|||
Flexural Strength | 82.0 MPa | 11900 psi | GB/9341 |
Zhejiang Juner PC/ABSz-4 Alloy Applications: Shell of Small Household Electric ApplianceInformation provided by Zhejiang Juner New Materials Co, Ltd. |