Kingfa PC-S609 Toughened PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Impact Modified |
| Manufacturer | Kingfa Sci. & Tech. Co. |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kingfa PC-S609 Toughened PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features:Good mechanical propertiesSuper high impact strengthGood weather resistanceHigh glossGood processing propertiesStress cracking propertiesApplications:OA and IT partsAutomobile accessoriesElectrical and electronic partsSwitch and plugHousehold applianceInformation Provided by Kingfa Sci. & Tech. Co., Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc @Temperature 23.0 °C |
1.19 g/cc @Temperature 73.4 °F |
ASTM D792 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm @Temperature 23.0 °C |
0.0050 - 0.0070 in/in @Temperature 73.4 °F |
ASTM D955 |
| Melt Flow | 12 - 16 g/10 min @Load 1.20 kg, Temperature 300 °C |
12 - 16 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 58.0 MPa | 8410 psi | 50mm/min; ASTM D638 |
| Elongation at Break | >= 60 % | >= 60 % | 50mm/min; ASTM D638 |
| Flexural Strength | 82.0 MPa | 11900 psi | 2mm/min; ASTM D790 |
| Flexural Modulus | 2.30 GPa | 334 ksi | 2mm/min; ASTM D790 |
| Izod Impact, Notched | >= 4.50 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
>= 8.43 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Izod Impact, Unnotched | NB @Thickness 3.20 mm, Temperature 23.0 °C |
NB @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 131 °C @Thickness 6.40 mm |
268 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C @Thickness 6.40 mm |
257 °F @Thickness 0.252 in |
ASTM D648 |
| Flammability, UL94 | V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
|
| V-2 @Thickness 3.20 mm |
V-2 @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | <= 275 °C | <= 527 °F | |
| Rear Barrel Temperature | 240 - 270 °C | 464 - 518 °F | Start Point: 240°C |
| Middle Barrel Temperature | 240 - 260 °C | 464 - 500 °F | Start Point: 235°C |
| Front Barrel Temperature | 250 - 260 °C | 482 - 500 °F | Start Point: 240°C |
| Melt Temperature | 240 - 280 °C | 464 - 536 °F | Start Point: 250°C |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | Start Point: 60°C |
| Drying Temperature | 100 - 115 °C @Time 10800 - 14400 sec |
212 - 239 °F @Time 3.00 - 4.00 hour |
Pre-dry |
| Back Pressure | 0.300 - 1.00 MPa | 43.5 - 145 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Speed | 60-90% | |
| Weather Resistance (delta E) | ASTM D4459; 200hr xenon lamp |
Users viewing this material also viewed the following:
- Polimeri Europa Greenflex® ML 50 Ethylene Vinyl Acetate Copolymer - Injection Molding, Compounding & Extrusion
- Honeywell ACLAR® Cx™ 8A Heat Sealable, Co-Extruded CTFE Film (discontinued **)
- Karina 651D10/1-C-IS White PVC Compound
- H.C. Starck Grade A Chromium Carbide, Cr3C2
- Mitsubishi Xantar® C CF 407 Polycarbonate/ABS Blend
- Solvay TECHNYL® A 218HP V30 Black 21N PA66, 30% glass fiber, DRY
- American Elements Yttrium Nanoparticles
- Chosun Refractories PT-150 Plastic Refractory
- Nye Lubricants 608 (SO) Synthetic Oil
Copyright © lookpolymers.com All Rights Reserved