SABIC Innovative Plastics LNP Thermocomp MX88073 PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp MX88073 PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* MX88073 is a compound based on Polypropylene resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183 |
| 1.15 g/cc | 0.0415 lb/in³ | ASTM D 792 | |
| Linear Mold Shrinkage, Flow | 0.0090 cm/cm @Time 86400 sec |
0.0090 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.0092 cm/cm @Time 86400 sec |
0.0092 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm @Time 86400 sec |
0.011 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.011 cm/cm @Time 86400 sec |
0.011 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 52.0 MPa | 7540 psi | ISO 527 |
| 53.0 MPa | 7690 psi | ASTM D 638 | |
| Tensile Strength, Yield | 52.0 MPa | 7540 psi | ISO 527 |
| 54.0 MPa | 7830 psi | ASTM D 638 | |
| Elongation at Break | 2.8 % | 2.8 % | ASTM D 638 |
| 3.0 % | 3.0 % | ISO 527 | |
| Elongation at Yield | 2.6 % | 2.6 % | ASTM D 638 |
| 2.7 % | 2.7 % | ISO 527 | |
| Tensile Modulus | 5.83 GPa | 846 ksi | 1 mm/min; ISO 527 |
| 6.756 GPa | 979.9 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 82.0 MPa | 11900 psi | ASTM D 790 |
| 85.0 MPa | 12300 psi | ISO 178 | |
| Flexural Modulus | 5.30 GPa | 769 ksi | ASTM D 790 |
| 6.00 GPa | 870 ksi | ISO 178 | |
| Izod Impact, Notched | 1.06 J/cm @Temperature 23.0 °C |
1.99 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 4.27 J/cm @Temperature 23.0 °C |
8.00 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 26.0 kJ/m² @Temperature 23.0 °C |
12.4 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 5.00 J | 3.69 ft-lb | Multiaxial Impact; ISO 6603 |
| 11.0 J @Temperature 23.0 °C |
8.11 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 84.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
46.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 84.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
47.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 43.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
24.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 44.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
24.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 153 °C | 307 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 156 °C @Thickness 3.20 mm |
313 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 261 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 132 °C @Thickness 3.20 mm |
270 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- Proto3000 Objet Digital Materials™ DM_8320 Rigid Opaque Prototyping Polymer
- SABIC Innovative Plastics Lexan® PC0700 PC (Asia Pacific)
- PolyOne Edgetek® PK-30CF/000 Polyetheretherketone (PEEK), Carbon Fiber Reinforced (discontinued **)
- NanoAmor 94%, OD/WT/L: 20-50/1-2 nm/0.5-2 um Multi-Walled Carbon Nanotubes
- LG Chemical LUMAX HF-5306F High Flow PBT, 30% Polymer Alloy, Weather Resistant, Flame Retardant
- Teknor Apex APEX® 124 Polyvinyl Chloride, Flexible
- Shamrock Technologies Fluoro T® 611 Thermoplastic Grade PTFE Additive
- Covestro Texin® 285 Urethane Thermoplastic Elastomer
- 3M Dyneon™ TF 5050Z PTFE
Copyright © lookpolymers.com All Rights Reserved