SABIC Innovative Plastics LNP STAT-KON PE002Z PA 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON PE002Z PA 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-KON* PE002Z is a compound based on Nylon 6 resin containing 10% Carbon Fiber. Added features of this grade include: Extrusion Grade.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | ISO 1183 |
| 1.18 g/cc | 0.0426 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.930 % | 0.930 % | 23°C / 50% RH; ISO 62 |
| 0.930 % | 0.930 % | 50% RH, 24 hrs; ASTM D570 | |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 58.0 MPa | 8410 psi | Type I, 5 mm/min; ASTM D638 |
| 59.0 MPa | 8560 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 10.8 % | 10.8 % | 5 mm/min; ISO 527 |
| 32 % | 32 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 0.210 GPa | 30.5 ksi | 50 mm/min; ASTM D638 |
| 0.870 GPa | 126 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 82.0 MPa | 11900 psi | ISO 178 |
| 121 MPa | 17500 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 2.13 GPa | 309 ksi | 2 mm/min; ISO 178 |
| 4.07 GPa | 590 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.850 J/cm | 1.59 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 13.05 J/cm | 24.45 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 65.0 kJ/m² | 30.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 11.0 J @Temperature 23.0 °C |
8.11 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 53.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
29.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 94.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
52.2 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C | 383 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 194 °C @Thickness 3.20 mm |
381 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 134 °C | 273 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 131 °C @Thickness 3.20 mm |
268 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 7.0 - 9.0 ohm | 7.0 - 9.0 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Ritelok PS67 Adhesive
- Rogers Corporation R/bak® SS Cushion Mounting Materials, Supported Soft
- Michelman® Coating X300™ Plus Water based, moisture and water resistant coating
- ChevronTexaco 22 Heat Transfer Oil
- ExxonMobil HDPE HD 6719.62 High Density Polyethylene Copolymer Resin
- AK Steel PH 15-7 Mo® Precipitation Hardening Stainless Steel, Condition CH 900
- ATI Allegheny Ludlum Stainless Steel Chromium-Nickel-Molybdenum 317LXN™ (UNS S31726)
- ATI Allvac® 706 Nickel Superalloy, Heat Treatment: 954°C (1750°F) + Age
- Hexcel® HexWeb® CR III 3/16-5052-.0025 Corrosion Resistant Specification Grade Aluminum Honeycomb
Copyright © lookpolymers.com All Rights Reserved