SABIC Innovative Plastics LNP STAT-LOY WF306C PBT

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP Stat-loy
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP STAT-LOY WF306C PBT.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* STAT-LOY* WF306C is a compound based on PBT resin containing 30% Glass Fiber. Added features of this material include: Antistat, Clean Compound System.
Physical Properties Metric English Comments
Density 1.48 g/cc
0.0535 lb/in³
ASTM D792
1.48 g/cc
0.0535 lb/in³
ISO 1183
Moisture Absorption 2.50 %
2.50 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.0039 cm/cm

@Time 86400 sec
0.0039 in/in

@Time 24.0 hour
ISO 294
0.0030 - 0.0050 cm/cm

@Time 86400 sec
0.0030 - 0.0050 in/in

@Time 24.0 hour
ASTM D955
Linear Mold Shrinkage, Transverse 0.010 - 0.012 cm/cm

@Time 86400 sec
0.010 - 0.012 in/in

@Time 24.0 hour
ASTM D955
0.011 cm/cm

@Time 86400 sec
0.011 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 62.0 MPa
8990 psi
ASTM D638
63.0 MPa
9140 psi
ISO 527
Tensile Strength, Yield 62.0 MPa
8990 psi
ASTM D638
63.0 MPa
9140 psi
ISO 527
Elongation at Break 1.7 %
1.7 %
ISO 527
2.0 %
2.0 %
ASTM D638
Elongation at Yield 1.7 %
1.7 %
ISO 527
2.0 %
2.0 %
ASTM D638
Tensile Modulus 6.65 GPa
965 ksi
1 mm/min; ISO 527
7.58 GPa
1100 ksi
50 mm/min; ASTM D638
Flexural Strength 82.0 MPa
11900 psi
ASTM D790
93.0 MPa
13500 psi
ISO 178
Flexural Modulus 5.51 GPa
799 ksi
ASTM D790
5.60 GPa
812 ksi
ISO 178
Izod Impact, Notched 0.900 J/cm
1.69 ft-lb/in
ASTM D256
Izod Impact, Unnotched 6.08 J/cm
11.4 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 9.00 kJ/m²
4.28 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 34.0 kJ/m²
16.2 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 13.0 J
9.59 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 3.00 J
2.21 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 124 µm/m-°C

@Temperature -40.0 - 40.0 °C
68.9 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
125 µm/m-°C

@Temperature -40.0 - 40.0 °C
69.4 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 59.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
33.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
60.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
33.3 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 207 °C
405 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
210 °C

@Thickness 3.20 mm
410 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 172 °C
342 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
177 °C

@Thickness 3.20 mm
351 °F

@Thickness 0.126 in
unannealed; ASTM D648