SABIC PS 126 General Purpose Polystyrene for Injection Molding

Category	Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Transparent Grade
Manufacturer	SABIC
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC PS 126 General Purpose Polystyrene for Injection Molding.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: General purpose Polystyrene PS 125 is manufactured by continuous mass polymerization of styrene monomer. It is a crystal-like, hard and brittle polymer with medium flow and high clarity. It also has medium Vicat and heat deflection temperatures making it suitable for various applications.Typical Applications: It is recommended for the manufacture of packaging items, namely jewelry and gift boxes; medical supplies such as Petri dishes, test tubes holders and specimen jars. It can also be used in capping the high impact polystyrene coextruded sheet for higher surface gloss and can be blended with impact modifier resin for clear packaging articles.Information provided by SABIC.

Physical Properties	Metric	English	Comments
Bulk Density	0.600 g/cc	0.0217 lb/in³	ASTM D1895B
Density	1.05 g/cc	0.0379 lb/in³	Load Density; ASTM D792
Melt Flow	7.0 g/10 min @Load 2.16 kg, Temperature 230 °C	7.0 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell L	95	95	ASTM D785
Hardness, Rockwell M	63	63	ASTM D785
Tensile Strength at Break	43.0 MPa	6240 psi	ASTM D638
Elongation at Break	2.0 %	2.0 %	ASTM D638
Tensile Modulus	2.598 GPa	376.8 ksi	ASTM D638
Flexural Strength	82.0 MPa	11900 psi	ASTM D790
Flexural Modulus	3.529 GPa	511.8 ksi	ASTM D790
Izod Impact, Notched	0.120 J/cm	0.225 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	90.0 °C	194 °F	ASTM D648
Vicat Softening Point	95.0 °C @Load 1.00 kg	203 °F @Load 2.20 lb	ASTM D1525B
Flammability, UL94	HB @Thickness 1.30 mm	HB @Thickness 0.0512 in
	HB @Thickness 3.00 mm	HB @Thickness 0.118 in

Users viewing this material also viewed the following: