Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 68.0 MPa | 9860 psi | ISO 178 |
Nilit FRIANYL B63 HS-GV 5 Nylon 6 for injection molding, 5% glass fiber reinforced Nylon 6 for injection molding, high impact modified.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Flexural Strength | 68.0 MPa | 9860 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP DBP32EI PC (Asia Pacific) LNP* Lubricomp* DBP32EI is a compound based on Polycarbonate resin containing PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive, Internally Lubricated. |
|||
Flexural Strength | 68.0 MPa | 9860 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP DL0039E PC LNP* Lubricomp* DL0039E is a compound based on Polycarbonate resin containing 15% PTFE. Added features of this material include: Internally Lubricated, Flame Retardant, Easy Molding. |
|||
Flexural Strength | 68.0 MPa | 9860 psi | ASTM D790 |
Ineos Nova Zylar® 330 Clear Impact Modified Acrylic Copolymer
(discontinued **) Features:Clarity and stiffness Good heat distortion resistance Styrenic processing advantages Excellent property retention after gamma and ETO sterilization Meets USP XXIII specifications for Class .. |
|||
Flexural Strength | 68.0 MPa | 9860 psi | 2mm/min; ASTM D790 |
Kingfa HR-527 Modified ABS Features:UL94 HB @ 1.5-3.2mmImpact resistanceApplications:Automobile partsAutomobile audioDashboard, interior trimAutomobile lamp, mirrorInformation Provided by Kingfa Sci. & Tech. Co., Ltd. |
|||
Flexural Strength | 68.0 MPa | 9860 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP DX94375H PC LNP* LUBRICOMP* DX94375H is a compound based on Polycarbonate resin containing Proprietary Fillers. Added features of this material include: Healthcare, Wear Resistant. |
|||
Flexural Strength | 68.0 MPa | 9860 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP KL002 Acetal Copoly (Asia Pacific) LNP* Lubricomp* KL002 is a compound based on Acetal Copolymer resin containing PTFE. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 68.0 MPa | 9860 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP OL009 PPS - Linear LNP LUBRICOMP* OL009 is a compound based on PPS - Linear resin containing 45% PTFE. Added features of this material include: Wear Resistant. |
|||
Flexural Strength | 68.0 MPa | 9860 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP OL009 PPS - Linear (Asia Pacific) LNP* LUBRICOMP* OL009 is a compound based on PPS - Linear resin containing PTFE. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 68.0 MPa | 9860 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP ZP001XXP PPE+PS (Asia Pacific) LNP* Lubricomp* ZP001XXP is a compound based on PPE+PS Blend resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 68.0 MPa | 9860 psi | ASTM D790 |
SABIC Innovative Plastics LNP STAT-KON AX06518 ABS LNP* STAT-KON* AX06518 is a compound based on ABS resin containing Stainless Steel. Added features of this material include: Electrically Conductive, Flame Retardant, EMI/RFI Shielding. |
|||
Flexural Strength | 68.0 MPa | 9860 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP AF001H ABS LNP* THERMOCOMP* AF001H is a compound based on ABS resin containing 5% Glass Fiber. Added feature of this material is: Healthcare. |
|||
Flexural Strength | 68.0 MPa | 9860 psi | ASTM D 790 |
SABIC Innovative Plastics LNP Thermocomp KB005 Acetal Copolymer LNP THERMOCOMP* KB005 is a compound based on Acetal Copolymer resin containing Glass Bead.This data was supplied by SABIC-IP for the Americas region. |
|||
Flexural Strength | 68.0 MPa | 9860 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP MF002AS PP (Asia Pacific) LNP* THERMOCOMP* MF002AS is a compound based on Polypropylene resin containing Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
Flexural Strength | 68.0 MPa | 9860 psi | ASTM D 790 |
SABIC Innovative Plastics LNP Thermocomp PH0600B PA 6 (Asia Pacific) LNP* Thermocomp* PH0600B is a compound based on Nylon 6 resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity.This data was supplied by SABIC.. |
|||
Flexural Strength | 68.0 MPa | 9860 psi | 3 points and 2 mm/min; ISO 178 |
Styron Magnumâ„¢ 3453 Acrylonitrile Butadiene Styrene (ABS) MAGNUMâ„¢ 3453 ABS is a general purpose injection molding resin suitable for a wide range of applications.Information provided by DowThis product line was spun off from Dow Chemical to Styron in .. |
|||
Flexural Strength | 68.0 MPa | 9860 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP WBL36L PBT LNP* LUBRICOMP* WBL36L is a compound based on PBT resin containing 30% Glass Bead, 15% PTFE. Added features of this material include: Wear Resistant, Low Extractible. |
|||
Flexural Strength | 68.0 MPa | 9860 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP DF004 PC LNP* THERMOCOMP* DF004 is a compound based on Polycarbonate resin containing 20% Glass Fiber. |
|||
Flexural Strength | 68.0 MPa | 9860 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP MFB429 PP LNP* THERMOCOMP* MFB429 is a compound based on Polypropylene resin containing 10% Glass Fiber, 20% Glass Bead. Added features of this material include: Chemically Coupled, Flame Retardant. |
|||
Flexural Strength | 68.0 MPa | 9860 psi | ASTM D790 |
Lubrizol Isoplast® 2510 Engineering Thermoplastic Polyurethane Resin Feature: USP Class VIAvailable in Americas, Europe, Middle East, Africa, India and AsiaData provided by LubrizolLubrizol acquired the Isoplast product line from Dow in 2009. |
|||
Flexural Strength | 68.0 MPa | 9860 psi | ISO 178 |
Denka TH-11 Transparent Resin Polymer (MBS resin) Polymethacrylate Butadiene Styrene "TX Polymer" (methyl methacrylate styrene), MS resins as an alternative to acrylic resins, with low density, low moisture absorption, and good moldability, "TH Polymer/TP Polymer," MBS resins with a.. |
|||
Flexural Strength | 68.0 MPa | 9860 psi | ISO 178 |
Denka TP-801 Transparent Resin Polymer (MBS resin) Polymethacrylate Butadiene Styrene "TX Polymer" (methyl methacrylate styrene), MS resins as an alternative to acrylic resins, with low density, low moisture absorption, and good moldability, "TH Polymer/TP Polymer," MBS resins with a.. |
|||
Flexural Strength | 68.0 MPa @Temperature 23.0 °C |
9860 psi @Temperature 73.4 °F |
EN ISO 178 |
Ensinger TECASINT 3032 Polyimide, Black, 40% Graphite (PI) TECASINT is a range of non-melting high temperature polyimides characterized by high strength over a wide range of temperatures, good long term thermal stability, minimal thermal expansion and excel.. |
|||
Flexural Strength | 68.0 MPa | 9860 psi | 2 mm/min; ISO 178 |
Chi Mei Polyrex® PG-80 Polystyrene High strength |
|||
Flexural Strength | 68.0 MPa | 9860 psi | ISO 178 |
Azoty Tarnow™ TARNOFORM 411 POM Easy flowing, internally strengthened grade for injection molding of thin walled parts of very high mechanical requirements.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A. |
|||
Flexural Strength | 68.0 MPa | 9860 psi | ISO 178 |
Azoty Tarnow™ TARNOFORM 500 POM Easy flowing grade for injection molding of thin-walled parts or in case of long flow path.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A. |
|||
Flexural Strength | 68.0 MPa | 9860 psi | ASTM D790 |
A. Schulman ComAlloy Comtuf® 525 Polycarbonate/Styrenic Alloy Data provided by the manufacturer, ComAlloy International Company. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been integrated into the A Sc.. |
|||
Flexural Strength | 68.0 MPa | 9860 psi | ASTM D790 |
A. Schulman ComAlloy Hiloy® 131 Polypropylene, Glass/Mineral Reinforced, Chemically Coupled Data provided by the manufacturer, ComAlloy International Company.50% Glass/Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |