SABIC Innovative Plastics LNP Thermocomp KB005 Acetal Copolymer
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Glass Bead Filled |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp KB005 Acetal Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* KB005 is a compound based on Acetal Copolymer resin containing Glass Bead.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.59 g/cc | 0.0574 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.19 % | 0.19 % | 23°C / 50% RH; ISO 62 |
| 0.10 % @Time 86400 sec |
0.10 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.023 cm/cm @Time 86400 sec |
0.023 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.0233 cm/cm @Time 86400 sec |
0.0233 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.022 cm/cm @Time 86400 sec |
0.022 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.0224 cm/cm @Time 86400 sec |
0.0224 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 23.0 MPa | 3340 psi | ISO 527 |
| 37.0 MPa | 5370 psi | ASTM D 638 | |
| Elongation at Break | 12 % | 12 % | ISO 527 |
| 17 % | 17 % | ASTM D 638 | |
| Tensile Modulus | 3.70 GPa | 537 ksi | 1 mm/min; ISO 527 |
| 3.72 GPa | 540 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 68.0 MPa | 9860 psi | ASTM D 790 |
| 77.0 MPa | 11200 psi | ISO 178 | |
| Flexural Modulus | 2.89 GPa | 419 ksi | ASTM D 790 |
| 3.30 GPa | 479 ksi | ISO 178 | |
| Izod Impact, Notched | 0.900 J/cm @Temperature 23.0 °C |
1.69 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 2.93 J/cm @Temperature 23.0 °C |
5.49 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² @Temperature 23.0 °C |
1.43 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 27.0 kJ/m² @Temperature 23.0 °C |
12.8 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| 7.00 J @Temperature 23.0 °C |
5.16 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C | 219 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 112 °C @Thickness 3.20 mm |
234 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- SABIC 6318B Linear Low Density Polyethylene for Cast Film
- Polykemi AB POLYelast TPE ED80 D40 UV Thermoplastic Elastomer
- Quantum Composites HTC-9500 55% E-Glass Fiber Reinforced Bismaleimide SMC, High Temperature Composite
- Samsung Cheil Industries Infino® HI-1001BP PC/ABS, Metal Plating Grade
- SABIC Innovative Plastics LNP THERMOCOMP WC006 PBT (Europe-Africa-Middle East)
- 3M 5490 PTFE Extruded Film Tape
- China-Yixing Longly Refractories 75 Alumina Ceramic
- PolyOne Synprene® IT 705 Thermoplastic Elastomer - SBC (discontinued **)
- Austin Novel Materials Texalan® 695A Polyester and Polyether based TPU
Copyright © lookpolymers.com All Rights Reserved