SABIC Innovative Plastics LNP THERMOCOMP DF004 PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP DF004 PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* DF004 is a compound based on Polycarbonate resin containing 20% Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ASTM D792 |
| 1.35 g/cc | 0.0488 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Time 86400 sec |
0.0020 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0020 cm/cm @Time 86400 sec |
0.0020 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0045 cm/cm @Time 86400 sec |
0.0045 in/in @Time 24.0 hour |
ISO 294 |
| 0.0050 cm/cm @Time 86400 sec |
0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 91.0 MPa | 13200 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 9.5 % | 9.5 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 5.51 GPa | 799 ksi | 50 mm/min; ASTM D638 |
| 5.94 GPa | 862 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 68.0 MPa | 9860 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 5.51 GPa | 799 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 1.33 J/cm | 2.49 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 9.61 J/cm | 18.0 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 59.0 kJ/m² | 28.1 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 144 °C @Thickness 3.20 mm |
291 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 141 °C | 286 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 139 °C @Thickness 3.20 mm |
282 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- NanoAmor 95%, OD: < 8 nm COOH Functionalized Aligned Multi-Walled Carbon Nanotubes
- PolyOne Geon™ Vinyl Flexible R4510H Polyvinyl Chloride, Flexible (PVC, Flexible)
- Overview of materials for Nylon 66, 40% Glass Fiber Filled
- Lucite International Elvacite ® 4409 Acrylic Resin, Hydroxyl Functional
- Vesta Ceramics SicoNide® P Silicon Nitride Powder
- A. Schulman FORMION™ FI 335 Ionomer
- E-Polymers TEKASTER® F101FR Un-Reinforced Flame Retardant PBT
- 3M Scotchcal™ 8000-15 Graphic Film
- 3M 973
Copyright © lookpolymers.com All Rights Reserved