Ensinger TECASINT 3032 Polyimide, Black, 40% Graphite (PI)

Category Polymer , Thermoplastic , Polyimide, Thermoplastic , Thermoplastic Polyimide, Graphite Filled
Manufacturer Ensinger
Trade Name TECASINT
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ensinger TECASINT 3032 Polyimide, Black, 40% Graphite (PI).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
TECASINT is a range of non-melting high temperature polyimides characterized by high strength over a wide range of temperatures, good long term thermal stability, minimal thermal expansion and excellent wear resistance among other things. The TECASINT 2000 series offers these enhanced thermal properties along with lower moisture absorption, a higher degree of toughness, and better machining properties. TECASINT 2011 is unfilled, while TECASINT 2021 contains 15% graphite which offer improved wear resistance and a lower coefficient of friction. TECASINT 2000 series with their superior physical properties, are ideal for application in the aerospace, nuclear, automotive, electrical/electronics, and chemical processing industries.Main features: High thermal and mechanical capacity, very creep resistant, good radiation-resistance, good sliding properties, broad chemical compatibility, low thermal expansion, no electrical insulation, sensitive to hydrolysis in higher thermal range, flame retardant according to UL94 V-0, low water absorption, high toughnessApplications: Mechanical engineering, automotive industry, materials handling equipment, hot glass technology, aircraft and aerospace industries, cryogenics, precision engineering, textile industryPreferred Fields: Valve seating, piston rings, chain guides, gripper finger for hot glass, bearing discs, washers, bushingsInformation Provided by Ensinger Sintimid
Physical Properties Metric English Comments
Density 1.49 g/cc
0.0538 lb/in³
DIN 53 479
Water Absorption 0.54 %

@Temperature 23.0 °C
0.54 %

@Temperature 73.4 °F
24 hours in water; EN ISO 62
3.15 %

@Temperature 80.0 °C
3.15 %

@Temperature 176 °F
24 hours in water; EN ISO 62
Mechanical Properties Metric English Comments
Hardness, Shore D 80

@Temperature 23.0 °C
80

@Temperature 73.4 °F
DIN 53 505
Tensile Strength 41.6 MPa

@Temperature 23.0 °C
6030 psi

@Temperature 73.4 °F
EN ISO 527
Elongation at Break 2.2 %

@Temperature 23.0 °C
2.2 %

@Temperature 73.4 °F
EN ISO 527
Elongation at Yield 2.2 %

@Temperature 23.0 °C
2.2 %

@Temperature 73.4 °F
Flexural Elongation; EN ISO 178
Tensile Modulus 3.524 GPa

@Temperature 23.0 °C
511.1 ksi

@Temperature 73.4 °F
EN ISO 527
Flexural Strength 68.0 MPa

@Temperature 23.0 °C
9860 psi

@Temperature 73.4 °F
EN ISO 178
Flexural Modulus 3.865 GPa

@Temperature 23.0 °C
560.6 ksi

@Temperature 73.4 °F
EN ISO 178
Compressive Yield Strength 87.0 MPa

@Strain 10.0 %,
Temperature 23.0 °C
12600 psi

@Strain 10.0 %,
Temperature 73.4 °F
EN ISO 604
Compressive Strength 133 MPa

@Temperature 23.0 °C
19300 psi

@Temperature 73.4 °F
EN ISO 604
Compressive Modulus 1.044 GPa

@Temperature 23.0 °C
151.4 ksi

@Temperature 73.4 °F
EN ISO 604
Charpy Impact Unnotched 1.07 J/cm²

@Temperature 23.0 °C
5.09 ft-lb/in²

@Temperature 73.4 °F
EN ISO 179
Charpy Impact, Notched 0.300 J/cm²

@Temperature 23.0 °C
1.43 ft-lb/in²

@Temperature 73.4 °F
EN ISO 179
Compression Set 29 %

@Temperature 23.0 °C
29 %

@Temperature 73.4 °F
Compression at Break; EN ISO 604
Thermal Properties Metric English Comments
CTE, linear 31.0 µm/m-°C

@Temperature 50.0 - 200 °C
17.2 µin/in-°F

@Temperature 122 - 392 °F
DIN 53 752
40.0 µm/m-°C

@Temperature 200 - 300 °C
22.2 µin/in-°F

@Temperature 392 - 572 °F
DIN 53 752