Polymer Property : Flexural Strength = 50.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	<= 50.0 MPa	<= 7250 psi	ISO 178
Polykemi AB POLYfill PPH GK8040 Polypropylene Homopolymer, Glass Reinforced Information provided by Polykemi AB
Flexural Strength	50.0 MPa	7250 psi	ISO 178
Nilit FRIANYL A63 TF30 Nylon 6.6 for injection molding, 30% PTFE lubricated Nylon 6.6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Flexural Strength	<= 50.0 MPa	<= 7250 psi	ISO 178
Polykemi AB SCANLON A 5005B UV PA/ABS-Blend Information provided by Polykemi AB
Flexural Strength	50.0 MPa	7250 psi	Transverse
Quadrant Plastic Composites MultiQ® Impact Thermoplastic Panel Composite MultiQ is a product line of thermoplastic composites in panel form whose specific properties make them particularly suitable as an environmental alternative to plywood in outdoor applications. Howev..
Flexural Strength	50.0 - 60.0 MPa	7250 - 8700 psi	ISO 178
Raschig Group EN 5004 Epoxy Molding Compound Mica reinforced molding compound. Low mold shrinkage and post-shrinkage, very good electrical values, outstanding heat resistance, very goo pourablity. This product meets the allowed upper limits fo..
Flexural Strength	50.0 MPa @Temperature 121 °C	7250 psi @Temperature 250 °F	ASTM D790
Penn Fibre Pennite® 4512 Nylon 6, 12% Glass Fiber Reinforced (PA6) PENNITE® 4512 is a 12% glass fiber reinforced, black pigmented, thermally modified, type 6 nylon, available in sheets and rolls for high performance thermoforming and fabrication applications. PENN..
Flexural Strength	50.0 MPa	7250 psi	ISO 178
Nilit FRIANYL B63 H Nylon 6 for injection molding Nylon 6 for injection molding, heat stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Flexural Strength	50.0 MPa	7250 psi	1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics LNP Stat-loy AX06484X ABS LNP* Stat-Loy* AX06484 is a compound based on ABS resin containing mineral filler. Characteristics of this grade is it is extrudeable and static dissipative.This data was supplied by SABIC-IP for t..
Flexural Strength	50.0 MPa	7250 psi	Bending Strength
Saint-Gobain SpectrosilÂ® 1000 Optical Fused Quartz SpectrosilÂ® 1000 grade is used for non-transmissive mirrors and substrates, and other high purity components which do not require specified optical transmission.SpectrosilÂ® is a synthetic fuse..
Flexural Strength	50.0 MPa	7250 psi	Bending Strength
Saint-Gobain SpectrosilÂ® 2100 Optical Fused Quartz SpectrosilÂ® 2100 has improved refractive index homogeneity.SpectrosilÂ® is a synthetic fused silica manufactured using a patented, environmentally friendly process that results in a virtually c..
Flexural Strength	50.0 MPa	7250 psi	Bending Strength
Saint-Gobain VitreosilÂ® 055 Optical Fused Quartz VitreosilÂ® 055 is the highest grade of optical grade fused quartz available from Saint-Gobain Quartz for use in the near UV and visible. It has a useful transmission range from 270 nm in the nea..
Flexural Strength	50.0 MPa	7250 psi
Sapco C 410 Steatite Information provided by Sapco.
Flexural Strength	50.0 MPa	7250 psi	Bending Strength
Saint-Gobain PuropsilÂ® B Infrared Grade Low [OH] Optical Fused Quartz PuropsilÂ® B optical infrared fused quartz is manufactured from naturally occurring quartz crystal using a plasma process to ensure a low OH. It has excellent IR transmission with a useful IR tra..
Flexural Strength	50.0 MPa	7250 psi	ASTM D790
Polyram RamOfin PPH313V4 Polypropylene, 20% Mineral Filled 20% mineral filled, impact modified polypropylene for injection molding applicationsInformation provided by Polyram Ram On Ind.
Flexural Strength	50.0 MPa	7250 psi	ISO 178-93
Wellman Wellamid® XT1627-BK2 High Impact Nylon 66 Description: High Impact Nylon 66Information provided by Wellman.
Flexural Strength	50.0 MPa	7250 psi	GB/9341
Zhejiang Juner JEPPA003 High Glossy PP Applications: High Glossy PartsInformation provided by Zhejiang Juner New Materials Co, Ltd.
Flexural Strength	50.0 MPa	7250 psi	ASTM D790
A. Schulman POLYFLAM™ RABS 930-01 Information provided by A. Schulman.
Flexural Strength	50.0 MPa	7250 psi
Chengdu Polyster PPHA p-Hydroxybenzoic Acid Polymer PPHA is difficult to manufacture and brittle as well as low mechanical strength, its compounds have a higher mechanical strength and can be injection moulded. It can work without oil and its perform..
Flexural Strength	50.0 MPa	7250 psi	cond; ISO 178
DSM EcoPaXX® Q-X07290 PA410-I Impact Modified
Flexural Strength	50.0 MPa	7250 psi	ISO 178
DuPont Performance Polymers Crastin® ST820 NC010 Polybutylene Terephthalate (PBT) (Unverified Data**) Unreinforced Polybutylene Terephthalate with Excellent Impact Resistance Crastin ST820 NC010 is an unreinforced Super Tough polybutylene terephthalate resin for injection molding.Information provide..
Flexural Strength	50.0 MPa	7250 psi	After conditioning at 23°C and 50% RH; ISO 178
Arkema Group Orgalloy® RS 60E10 Polyamide Alloy Polyamide Alloy, Rigid Blown film gradeTubes / Mandrels / Profiles / CablesInformation provided by Arkema Group
Flexural Strength	50.0 MPa	7250 psi	ASTM D790
Aclo Accutech Polypropylene HP0335T40V Homopolymer Talc Reinforced Approved to ESF-M4D355B White B12391
Flexural Strength	50.0 MPa	7250 psi	ISO 178
Ascend Performance Materials Vydyne® R220 Nylon 66, 40% mineral reinforced, Conditioned Vydyne® R220 is a 40% mineral-reinforced PA66 resin formulated for improved impact strength. Available in natural, it is an injection-molding grade formulated to retain the inherent processing adva..
Flexural Strength	<= 50.0 MPa	<= 7250 psi	ISO 178
Polykemi AB POLYfill PPH T8020 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB
Flexural Strength	<= 50.0 MPa	<= 7250 psi	ISO 178
Polykemi AB POLYfill PPH TS15030 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB
Flexural Strength	50.0 MPa	7250 psi	ISO 178
BASF Ultramid® B3M6 BK60564 30% Mineral Filled PA6 (Conditioned) Ultramid B3M6 BK60564 is a 30% mineral reinforced, pigmented black injection molding PA6 grade for industrial items requiring high impact strength and very high dimensional stability, excellent lase..
Flexural Strength	50.0 MPa	7250 psi	ISO 178
BASF Ultramid® B3M6 Grey 22319 Q94 30% Mineral Filled PA6 (Conditioned) Description: 30% Mineral-filled injection molding grade for high impact industrial items having very high dimensional stability, such as automobile wheel covers.Information provided by BASF
Flexural Strength	50.0 MPa	7250 psi	ASTM D790
Ineos Nova Zyntar® 702 High Performance Flame Retardant Polystyrene (discontinued **) Custom ColorsApplications: Injection molding, Gas-assist injection moldingThis is an impact grade of polystyrene containing chemicals to increase resistance to ignition in laboratory flame tests. L..