Arkema Group Orgalloy® RS 60E10 Polyamide Alloy
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | Arkema |
| Trade Name | Orgalloy® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arkema Group Orgalloy® RS 60E10 Polyamide Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyamide Alloy, Rigid Blown film gradeTubes / Mandrels / Profiles / CablesInformation provided by Arkema Group
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in³ | ISO R1183 |
| Water Absorption | 1.1 % | 1.1 % | 23°C / 24 hrs; ISO 62 |
| Moisture Absorption at Equilibrium | 1.3 % | 1.3 % | 23°C / 50% RH; ISO 62 |
| 3.2 % | 3.2 % | in 23°C water; ISO 62 | |
| Melt Flow | 14 g/10 min @Load 5.00 kg, Temperature 235 °C |
14 g/10 min @Load 11.0 lb, Temperature 455 °F |
after drying; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 71 | 71 | ISO 868 |
| Tensile Strength, Ultimate | 45.0 MPa | 6530 psi | ISO R527 |
| Tensile Strength, Yield | 42.0 MPa | 6090 psi | ISO R527 |
| Elongation at Break | 240 % | 240 % | ISO R527 |
| Elongation at Yield | 3.9 % | 3.9 % | ISO R527 |
| Modulus of Elasticity | 1.62 GPa | 235 ksi | ISO R527 |
| Flexural Strength | 50.0 MPa | 7250 psi | After conditioning at 23°C and 50% RH; ISO 178 |
| 61.0 MPa | 8850 psi | Dry; ISO 178 | |
| Flexural Modulus | 1.35 GPa | 196 ksi | After conditioning at 23°C and 50% RH; ISO 178 |
| 1.85 GPa | 268 ksi | Dry; ISO 178 | |
| Charpy Impact, Notched | 3.20 J/cm² | 15.2 ft-lb/in² | After conditioning at 23°C/50%RH; ISO 179/Af |
| 2.30 J/cm² @Temperature -20.0 °C |
10.9 ft-lb/in² @Temperature -4.00 °F |
Dry; ISO 179/Af | |
| 2.50 J/cm² @Temperature -20.0 °C |
11.9 ft-lb/in² @Temperature -4.00 °F |
After conditioning at 23°C/50%RH; ISO 179/Af | |
| 2.70 J/cm² @Temperature 23.0 °C |
12.8 ft-lb/in² @Temperature 73.4 °F |
Dry; ISO 179/Af |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 110 µm/m-°C @Temperature 20.0 - 60.0 °C |
61.1 µin/in-°F @Temperature 68.0 - 140 °F |
TMS2 Perkin Elmer |
| CTE, linear, Transverse to Flow | 140 µm/m-°C @Temperature 20.0 - 60.0 °C |
77.8 µin/in-°F @Temperature 68.0 - 140 °F |
TMS2 Perkin Elmer |
| Melting Point | 220 °C | 428 °F | ISO R1218 |
| Deflection Temperature at 0.46 MPa (66 psi) | 90.0 °C | 194 °F | ISO R75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ISO R75 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.60e+15 ohm-cm | 1.60e+15 ohm-cm | ASTM D257 |
| Surface Resistance | 4.90e+15 ohm | 4.90e+15 ohm | ASTM D257 |
| Dielectric Strength | 38.0 kV/mm @Thickness 1.00 mm |
965 kV/in @Thickness 0.0394 in |
ASTM D149 |
| Dissipation Factor | 0.025 @Frequency 100000 Hz |
0.025 @Frequency 100000 Hz |
NFC 26 230 |
| 0.070 @Frequency 100 Hz |
0.070 @Frequency 100 Hz |
NFC 26 230 | |
| 0.070 @Frequency 1000 Hz |
0.070 @Frequency 1000 Hz |
NFC 26 230 | |
| Comparative Tracking Index | >= 600 V | >= 600 V | NFC 26 220 |
Users viewing this material also viewed the following:
- LyondellBasell Integrateâ„¢ NE542013 Functionalized Polyolefin
- Karina E 10/31-RG-GE White Color Concentrate for PVC
- Wellman Wellamid® GFX1624-BK(PTFE) 30% Glass Fiber Reinforced, Lubricated Nylon 66
- Hexcel® HexPly® M35-4 80-180°C Curing Epoxy Matrix, M35-4/40%/48280/1000 Fabric
- Eastman Aspira EN177 Copolyester Resin for Extrusion Blow Molding
- Eurostar Staramide BG7HU PA6, 35% Glass Fiber Filled, Heat and UV Stabilized, Injection Molded
- Fainplast Compounds GS 7080 Flexible PVC, Electrical Plugs
- 3M Scotchcal™ ElectroCut™ 404 Graphic Film
- DSM Arnitel® EL630 Polyether Ester Elastomer (European and Asian Grade)
Copyright © lookpolymers.com All Rights Reserved