Polykemi AB SCANLON A 5005B UV PA/ABS-Blend

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS)/Nylon Blend , Nylon
Manufacturer Polykemi AB
Trade Name SCANLON A
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polykemi AB SCANLON A 5005B UV PA/ABS-Blend.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Polykemi AB
Physical Properties Metric English Comments
Density 1.05 g/cc
0.0379 lb/in³
ISO 1183
Linear Mold Shrinkage 0.0090 cm/cm
0.0090 in/in
With Flow; ISO 2577
0.0090 cm/cm
0.0090 in/in
Across Flow; ISO 2577
Melt Index of Compound 7.5 g/10 min

@Load 5.00 kg,
Temperature 240 °C
 7.5 g/10 min

@Load 11.0 lb,
Temperature 464 °F
 ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 64

@Time 15.0 sec
 64

@Time 0.00417 hour
 ASTM D2240
Tensile Strength at Break <= 40.0 MPa
<= 5800 psi
ISO/R527
Elongation at Break >= 150 %
>= 150 %
ISO/R527
Flexural Strength <= 50.0 MPa
<= 7250 psi
ISO 178
Flexural Modulus 1.40 GPa

@Temperature 23.0 °C
 203 ksi

@Temperature 73.4 °F
 ISO 178
Charpy Impact, Notched 4.50 J/cm²

@Temperature 23.0 °C
 21.4 ft-lb/in²

@Temperature 73.4 °F
 ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 90.0 °C
194 °F
120°C/h; ISO 75/1
Deflection Temperature at 1.8 MPa (264 psi) 60.0 °C
140 °F
120°C/h; ISO 75/1
Vicat Softening Point 105 °C

@Load 5.001 kg
 221 °F

@Load 11.03 lb
 50°C/h; ISO 306
185 °C

@Load 1.00 kg
 365 °F

@Load 2.21 lb
 50°C/h; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
Glow Wire Test 650 °C

@Thickness 2.00 mm
 1200 °F

@Thickness 0.0787 in
 IEC 695-2-1