SABIC Innovative Plastics LNP Stat-loy AX06484X ABS

Category Polymer , Thermoplastic , ABS Polymer
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP Stat-loy
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Stat-loy AX06484X ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Stat-Loy* AX06484 is a compound based on ABS resin containing mineral filler. Characteristics of this grade is it is extrudeable and static dissipative.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Density 1.39 g/cc
0.0502 lb/in³
ASTM D 792
Moisture Absorption at Equilibrium 5.6 %
5.6 %
23°C / 50% RH; ISO 62
3.8 %

@Time 86400 sec
 3.8 %

@Time 24.0 hour
 50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm

@Time 86400 sec
 0.0040 - 0.0060 in/in

@Time 24.0 hour
 ASTM D 955
Linear Mold Shrinkage, Transverse 0.0050 - 0.0070 cm/cm

@Time 86400 sec
 0.0050 - 0.0070 in/in

@Time 24.0 hour
 ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 25.0 MPa
3630 psi
Type I, 5 mm/min; ASTM D 638
26.0 MPa
3770 psi
5 mm/min; ISO 527
Tensile Strength, Yield 26.0 MPa
3770 psi
5 mm/min; ISO 527
28.0 MPa
4060 psi
Type I, 5 mm/min; ASTM D 638
Elongation at Break 2.1 %
2.1 %
5 mm/min; ISO 527
2.6 %
2.6 %
Type I, 5 mm/min; ASTM D 638
Elongation at Yield 2.1 %
2.1 %
5 mm/min; ISO 527
2.6 %
2.6 %
Type I, 5 mm/min; ASTM D 638
Tensile Modulus 2.54 GPa
368 ksi
1 mm/min; ISO 527
3.12 GPa
453 ksi
50 mm/min; ASTM D 638
Flexural Strength 45.0 MPa
6530 psi
ISO 178
50.0 MPa
7250 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Yield Strength 51.0 MPa
7400 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 2.59 GPa
376 ksi
2 mm/min; ISO 178
2.75 GPa
399 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 0.440 J/cm

@Temperature 23.0 °C
 0.824 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Unnotched 4.41 J/cm

@Temperature 23.0 °C
 8.26 ft-lb/in

@Temperature 73.4 °F
 ASTM D 4812
Izod Impact, Notched (ISO) 4.00 kJ/m²

@Temperature 23.0 °C
 1.90 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 25.0 kJ/m²

@Temperature 23.0 °C
 11.9 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1U
Impact Test 1.00 J
0.738 ft-lb
Multiaxial Impact; ISO 6603
3.00 J

@Temperature 23.0 °C
 2.21 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 95.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
 52.8 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D 696
CTE, linear, Transverse to Flow 62.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
 34.4 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D 696
Deflection Temperature at 0.46 MPa (66 psi) 93.0 °C
199 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
97.0 °C

@Thickness 3.20 mm
 207 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 76.0 °C
169 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
76.0 °C

@Thickness 3.20 mm
 169 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Electrical Properties Metric English Comments
Surface Resistance 7.0 - 9.0 ohm
7.0 - 9.0 ohm
ASTM D 257