BASF Ultramid® B3M6 Grey 22319 Q94 30% Mineral Filled PA6 (Conditioned)

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Mineral Filled
Manufacturer	BASF
Trade Name	Ultramid®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Ultramid® B3M6 Grey 22319 Q94 30% Mineral Filled PA6 (Conditioned).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: 30% Mineral-filled injection molding grade for high impact industrial items having very high dimensional stability, such as automobile wheel covers.Information provided by BASF

Physical Properties	Metric	English	Comments
Bulk Density	0.500 - 0.800 g/cc	0.0181 - 0.0289 lb/in³
Density	1.36 g/cc	0.0491 lb/in³	ISO 1183
Water Absorption	5.9 - 6.5 %	5.9 - 6.5 %	ISO 62
Moisture Absorption at Equilibrium	2.2 - 2.6 %	2.2 - 2.6 %	ISO 62
Viscosity Measurement	145	145	ISO 307
Linear Mold Shrinkage	0.0075 cm/cm	0.0075 in/in
Melt Flow	81.6 g/10 min @Load 5.00 kg, Temperature 275 °C	81.6 g/10 min @Load 11.0 lb, Temperature 527 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	45.0 MPa	6530 psi	ISO 527-1/-2
Elongation at Break	45 %	45 %	ISO 527-1/-2
Tensile Modulus	1.70 GPa	247 ksi	ISO 527-1/-2
Flexural Strength	50.0 MPa	7250 psi	ISO 178
Flexural Modulus	1.40 GPa	203 ksi	ISO 178
Izod Impact, Notched (ISO)	15.0 kJ/m² @Temperature 23.0 °C	7.14 ft-lb/in² @Temperature 73.4 °F	ISO 180/1A
Charpy Impact Unnotched	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	ISO 179/1eU
Charpy Impact, Notched	1.80 J/cm² @Temperature 23.0 °C	8.57 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA
Tensile Creep Modulus, 1000 hours	800 MPa @Strain <=0.500 %	116000 psi @Strain <=0.500 %	ISO 899-1

Thermal Properties	Metric	English	Comments
Thermal Conductivity	0.310 W/m-K	2.15 BTU-in/hr-ft²-°F	DIN 52612-1
Melting Point	220 °C	428 °F	ISO 11357-1/-3
Maximum Service Temperature, Air	100 °C	212 °F	for 50% loss of tensile strength after 20000hr
	180 °C	356 °F
Decomposition Temperature	>= 300 °C	>= 572 °F

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+10 ohm-cm	1.00e+10 ohm-cm	IEC 60093
Surface Resistance	1.00e+10 ohm	1.00e+10 ohm	IEC 60093
Dielectric Constant	6.2 @Frequency 1.00e+6 Hz	6.2 @Frequency 1.00e+6 Hz	IEC 60250
Dissipation Factor	0.20 @Frequency 1.00e+6 Hz	0.20 @Frequency 1.00e+6 Hz	IEC 60250
Comparative Tracking Index	450 V	450 V	Test Solution A; IEC 60112

Processing Properties	Metric	English	Comments
Processing Temperature	80.0 °C	176 °F	Hopper Throat
Zone 1	260 °C	500 °F	Feed Zone
Zone 2	370 °C	698 °F	Compression
Zone 3	280 °C	536 °F	Metering-zone
Zone 4	280 °C	536 °F	Nozzle
Melt Temperature	270 - 290 °C	518 - 554 °F	Injection Molding/Extrusion
	280 °C	536 °F	Optimal
Mold Temperature	80.0 °C	176 °F	Optimal
	80.0 - 90.0 °C	176 - 194 °F	Injection Molding
Drying Temperature	80.0 °C	176 °F
Dry Time	4 hour	4 hour

Descriptive Properties	Value	Comments
Color	Grey 22319 Q94
Commercial Status	Europe
Ignition Temperature	>400°C	ASTM D1929
Peripheral screw speed	< 0.3 m/s