Aclo Accutech Polypropylene HP0335T40V Homopolymer Talc Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Talc Filler |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene HP0335T40V Homopolymer Talc Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Approved to ESF-M4D355B White B12391
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.29 g/cc | 0.0466 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | ASTM D955 |
| Melt Flow | 5.0 g/10 min | 5.0 g/10 min | ASTM D1238 |
| Ash | 39 - 45 % | 39 - 45 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 93 | 93 | ASTM D785 |
| Tensile Strength, Yield | 29.0 MPa | 4210 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Tensile Modulus | 3.499 GPa | 507.5 ksi | ASTM D638 |
| Flexural Strength | 50.0 MPa | 7250 psi | ASTM D790 |
| Flexural Modulus | 3.60 GPa | 522 ksi | ASTM D790 |
| Izod Impact, Notched | 0.267 J/cm | 0.500 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 124 °C | 255 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 77.8 °C | 172 °F |
Users viewing this material also viewed the following:
- Plastcom PLASTAMID® 610 BT N 32 C PA610
- Kinlead ML11 General Grade BOPP Matt Film (thickness: 15 µm)
- Meilian Chemical PE12077 WHITE MASTERBATCH
- Karina 600D18/136-A-IS-BZ Gray PVC Compound
- SABIC Innovative Plastics NORYL ZM3640 PPE+PS (Asia Pacific)
- Sekisui PIOCELAN LP-50E Moldable Polymer Foam
- SABIC Innovative Plastics Valox® 508 PBT (Europe-Africa-Middle East)
- Washington Penn Medium Impact Copolymer 40% Talc Filled
- 3M Scotch-Weld™ PR1500 Plastic and Rubber Instant Adhesive
- Lubriplate 110 Brake Lubricant Automotive Lubricant
Copyright © lookpolymers.com All Rights Reserved