Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Modulus of Elasticity | 1.70 GPa | 247 ksi | 50% RH |
Murtfeldt Murylon® A Nylon 66 This material combines the excellent properties of the Murylon® range with additional high tensile and compressive strength, increased wear resistance, and a lower level of moisture absorption than.. |
|||
Modulus of Elasticity | 1.70 GPa | 247 ksi | ISO 178 |
Premix Thermoplastics PRE-ELEC® ESD 7140 Static Dissipative Thermoplastic Compound PRE-ELEC® ESD 7140 is a static dissipative thermoplastic masterbatch based on ABS. The dissipative property is permanent and built into the polymer chain. PRE-ELEC® ESD 7140 has been developed for.. |
|||
Modulus of Elasticity | 1.70 - 2.00 GPa | 247 - 290 ksi | ASTM D638-04 |
Proto3000 Objet Digital Materials™ DM_7230 Transparent Prototyping Polymer Primary material: FullCure720Secondary material: TangoBlackDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to provide .. |
|||
Modulus of Elasticity | 1.70 - 2.30 GPa | 247 - 334 ksi | ASTM D638-04 |
Proto3000 Objet Digital Materials™ DM_8505Gray20 Rigid Opaque Prototyping Polymer Primary material: VeroWhitePlusSecondary material: TangoBlackPlusDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to pr.. |
|||
Modulus of Elasticity | 1.70 - 2.30 GPa | 247 - 334 ksi | ASTM D638-04 |
Proto3000 Objet Digital Materials™ DM_8505Gray25 Rigid Opaque Prototyping Polymer Primary material: VeroWhitePlusSecondary material: TangoBlackPlusDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to pr.. |
|||
Modulus of Elasticity | 1.70 - 2.30 GPa | 247 - 334 ksi | ASTM D638-04 |
Proto3000 Objet Digital Materials™ DM_8505Gray35 Rigid Opaque Prototyping Polymer Primary material: VeroWhitePlusSecondary material: TangoBlackPlusDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to pr.. |
|||
Modulus of Elasticity | 1.70 - 2.30 GPa | 247 - 334 ksi | ASTM D638-04 |
Proto3000 Objet Digital Materials™ DM_8505Gray40 Rigid Opaque Prototyping Polymer Primary material: VeroWhitePlusSecondary material: TangoBlackPlusDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to pr.. |
|||
Modulus of Elasticity | 1.70 - 2.86 GPa | 247 - 415 ksi | Average value: 2.49 GPa Grade Count:19 |
Overview of materials for Polybutylene Terephthalate (PBT), Extrusion Grade This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Extrusion Grade". Each property range of values reported is minimum an.. |
|||
Modulus of Elasticity | 1.70 - 48.3 GPa | 247 - 7000 ksi | Average value: 13.9 GPa Grade Count:561 |
Overview of materials for Polyphthalamide (PPA) This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide". Each property range of values reported is minimum and maximum values of appropriate Ma.. |
|||
Modulus of Elasticity | 1.70 - 2.70 GPa | 247 - 392 ksi | Average value: 2.27 GPa Grade Count:50 |
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded". Each property range of values reported i.. |
|||
Modulus of Elasticity | 1.70 - 4.86 GPa | 247 - 705 ksi | Average value: 3.21 GPa Grade Count:6 |
Overview of materials for High Density Polyethylene (HDPE), Wood Filled This property data is a summary of similar materials in the MatWeb database for the category "High Density Polyethylene (HDPE), Wood Filled". Each property range of values reported is minimum and ma.. |
|||
Modulus of Elasticity | 1.70 - 7.80 GPa @Temperature 60.0 - 150 °C |
247 - 1130 ksi @Temperature 140 - 302 °F |
Average value: 4.22 GPa Grade Count:6 |
Overview of materials for Nylon 6, Glass Fiber Filled, Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Glass Fiber Filled, Flame Retardant". Each property range of values reported is minimum and max.. |
|||
Modulus of Elasticity | 1.70 - 10.79 GPa @Temperature -100 - 200 °C |
247 - 1565 ksi @Temperature -148 - 392 °F |
Average value: 4.65 GPa Grade Count:9 |
Overview of materials for Nylon 6, Glass/Mineral Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Glass/Mineral Reinforced". Each property range of values reported is minimum and maximum values.. |
|||
Modulus of Elasticity | 1.70 - 10.0 GPa | 247 - 1450 ksi | Average value: 4.74 GPa Grade Count:75 |
Overview of materials for Nylon 66, Glass Bead Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Glass Bead Filled". Each property range of values reported is minimum and maximum values of ap.. |
|||
Modulus of Elasticity | 1.70 GPa | 247 ksi | MD; ExxonMobil Method |
ExxonMobil Label-Lyte™ 35LH247 OPP Film Product Description: A super white opaque, caviated BOPP film for Pressure Sensitive (PSA) labeling applications where superior optics are desired. LH247 also shows excellent performance on reel-fed.. |
|||
Modulus of Elasticity | 1.70 GPa | 247 ksi | MD; ExxonMobil Method |
ExxonMobil Label-Lyte™ 50LH247 OPP Film Product Description: A super white opaque, cavitated BOPP film for Pressure Sensitive (PSA) labeling applications where superior optics are desired. 50LH247 also shows excellent performances on reel.. |
|||
Modulus of Elasticity | 1.70 GPa | 247 ksi | MD; ExxonMobil Method |
ExxonMobil Label-Lyte™ 50LH538 Preliminary Data Sheet OPP Film Product Description: A super white opaque polypropylene film face stock with a proprietary caviated core providing high yield and excellent opacity. The coated print surface provides exceptional ink.. |
|||
Modulus of Elasticity | 1.70 GPa | 247 ksi | MD; ExxonMobil Method |
ExxonMobil Oppalyte™ 40MH247 OPP Film Product Description: A super white opaque, modified higher density, biaxially oriented polypropylene film. This opaque and stiff film is ideal for mono material requirements and it has been especial.. |
|||
Modulus of Elasticity | 1.70 GPa | 247 ksi | MD; ExxonMobil Method |
ExxonMobil Oppalyte™ 42AH748 OPP Film Product Description: A high barrier, high speed, super white opaque, modified higher density biaxially oriented polypropylene film, coated one side high barrier PVdC, one side very low temperature s.. |
|||
Modulus of Elasticity | 1.70 GPa | 247 ksi | MD; ExxonMobil Method |
ExxonMobil Oppalyte™ 42MH647 OPP Film Product Description: A super white opaque, modified higher density, biaxially oriented polypropylene film, acrylic coated two sides. It provides outstanding performance on all packaging machines.Ava.. |
|||
Modulus of Elasticity | 1.70 GPa | 247 ksi | MD; ExxonMobil Method |
ExxonMobil Oppalyte™ 50MH247 OPP Film Product Description: A super white opaque, modified higher density, biaxially oriented polypropylene film. This opaque and stiff film is ideal for mono material requirements and it has been especial.. |
|||
Modulus of Elasticity | 1.70 GPa | 247 ksi | MD; ExxonMobil Method |
ExxonMobil Oppalyte™ 52MH648 OPP Film Product Description: A high speed super white opaque, modified higher density, biaxially oriented polypropylene film, coated one side acrylic, one side very low temperature seal (VLTS) coating. VLTS.. |
|||
Modulus of Elasticity | 1.70 GPa | 247 ksi | ISO 527-2 |
BASF Ultraform® N2640 E4 POM Description: Is a POM + MBS, elastomer-modified injection-molding grade with high toughness and high weld line strength.Information provided by BASF |
|||
Modulus of Elasticity | 1.70 GPa | 247 ksi | 1 mm/min; ISO 527-1 |
Addcomp PRIEX® 20097 Maleic Anhydride Grafted PP homopolymer Fields of application: Functionalised polypropylene to be used as compatibiliser for polymer blends or coupling agent for glass fibre, wood flour, natural fibres, multilayer films, aluminium foils, .. |
|||
Modulus of Elasticity | 1.70 GPa | 247 ksi | MD; ExxonMobil Method |
ExxonMobil Oppalyte™ 30MD447 OPP Film Product Description: A coextruded super white opaque, modified higher density, biaxially oriented polypropylene film, heat sealable on both sides. This opaque and extremely stiff film is ideal for u.. |
|||
Modulus of Elasticity | 1.70 GPa | 247 ksi | MD; ExxonMobil Method |
ExxonMobil Oppalyte™ 35HM247 OPP Film Product Description: A super white opaque, modified higher density, biaxially oriented polypropylene film. This opaque and stiff film is ideal for mono material requirements and it has been especial.. |
|||
Modulus of Elasticity | 1.70 GPa | 247 ksi | MD; ExxonMobil Method |
ExxonMobil Oppalyte™ 40MD447 OPP Film Product Description: A coextruded super white opaque, modified higher density, biaxially oriented polypropylene film, heat sealable on both sides. This opaque and extremely stiff film is ideal for u.. |
|||
Modulus of Elasticity | 1.70 GPa | 247 ksi | ISO 527 |
BASF Ultramid® B3M6 BK60564 30% Mineral Filled PA6 (Conditioned) Ultramid B3M6 BK60564 is a 30% mineral reinforced, pigmented black injection molding PA6 grade for industrial items requiring high impact strength and very high dimensional stability, excellent lase.. |
|||
Modulus of Elasticity | 1.70 - 2.60 GPa | 247 - 377 ksi | Average value: 2.26 GPa Grade Count:5 |
Overview of materials for Acrylic, Impact Modified Sheet This property data is a summary of similar materials in the MatWeb database for the category "Acrylic, Impact Modified Sheet". Each property range of values reported is minimum and maximum values of.. |
|||
Modulus of Elasticity | 1.70 - 5.17 GPa | 247 - 750 ksi | Average value: 2.95 GPa Grade Count:46 |
Overview of materials for Polypropylene with 10% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 10% Glass Fiber Filler". Specific grades with glass content between 5% and 14% are in.. |