Addcomp PRIEX® 20097 Maleic Anhydride Grafted PP homopolymer

Category Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer Addcomp
Trade Name PRIEX®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Addcomp PRIEX® 20097 Maleic Anhydride Grafted PP homopolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Fields of application: Functionalised polypropylene to be used as compatibiliser for polymer blends or coupling agent for glass fibre, wood flour, natural fibres, multilayer films, aluminium foils, or mineral filled polypropylene.Examples: Compatibilising short-and long glass fibres and PP applications such as automotive applications (instrument panel carrier, front-end, door modules, etc.) and Wood filled polymer composites.Mode of action and advantages: PRIEX® 20097 is a polypropylene, grafted with a very high content of maleic anhydride. The grafted maleic anhydride introduces polarity to the polymer achieving compatibility between polyolefins and more polar polymers like EVOH.Advantages: Excellent mechanical properties, good cost / performance; Ultra low smell, low VOC and emissions; Excellent wetting properties as a result of very low viscosity (hyperfluid grade); Excellent coupling agent for shortand long glass filled polyolefins providing enhanced physical, mechanical and thermal properties; Excellent coupling agent for natural fibre reinforced polymer composites or wood flour reinforced polymer composites; Free flowing pellets; and Safe and easy handling.Food contact: PRIEX® 20097 composition meets the requirements of Commission Directive 2002/72/EC and further amendments.Information provided by Addcomp Polymer Additive Solutions
Physical Properties Metric English Comments
Oxidative Induction Time (OIT) 25 min

@Temperature 190 °C
25 min

@Temperature 374 °F
ISO 11357-6
Melt Flow 25 - 30 g/10 min

@Load 1.20 kg,
Temperature 190 °C
25 - 30 g/10 min

@Load 2.65 lb,
Temperature 374 °F
die 8/1; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 24.8 MPa
3600 psi
ISO 527-2
Elongation at Break 1.55 %
1.55 %
ISO 527-2
Modulus of Elasticity 1.70 GPa
247 ksi
1 mm/min; ISO 527-1
Thermal Properties Metric English Comments
Melting Point 160 - 164 °C
320 - 327 °F
ISO 11357-3
Crystallization Temperature 113 - 115 °C
235 - 239 °F
ISO 11357-3
Deflection Temperature at 0.46 MPa (66 psi) 116.3 °C
241.3 °F
ISO 75
Processing Properties Metric English Comments
Processing Temperature <= 280 °C
<= 536 °F
Descriptive Properties Value Comments
Appearance White or slightly yellow granules
Free Aleic Anhydride <50 mg/kg
Solvay method
Grafted Maleic Anhydride 0.45%
Solvay method