- ExxonMobil Oppalyte™ 35HM247 OPP Film
ExxonMobil Oppalyte™ 35HM247 OPP Film
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade |
| Manufacturer | Exxon Chemical |
| Trade Name | Oppalyte™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Oppalyte™ 35HM247 OPP Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: A super white opaque, modified higher density, biaxially oriented polypropylene film. This opaque and stiff film is ideal for mono material requirements and it has been especially designed for cold seal applications.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features:Excellent stiffness and flex resistanceOutstanding opacity, white background and reduced show-throughGood moisture barrierExceptional printability and receptivity to coatingsExcellent support for cold seal adhesionFeatures: Light BarrierApplications:BakeryBiscuits/Cookie/Crackers Confectionery, ChocolateConfectionery, GumConfectionery, SugarCrisps and SnacksDry Foods and Beverage Powders Frozen Food Household and DetergentsIce Cream Uses: HFFS Flexible Packaging Processing Method: Cold Seal Adhesive, Inner Web Adhesive Lamination, Inner Web Extrusion Lamination, Outer Web Adhesive Lamination, Solvent Flexographic Printing, Solvent Rotogravure Printing and Surface Print UnsupportedInformation provided by ExxonMobil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Vapor Transmission | 1.10 g/m²/day @Temperature 23.0 °C |
0.0710 g/100 in²/day @Temperature 73.4 °F |
85% RH; ExxonMobil Method |
| 4.97 g/m²/day @Temperature 38.0 °C |
0.320 g/100 in²/day @Temperature 100 °F |
90% RH; ExxonMobil Method | |
| Thickness | 35.6 microns | 1.40 mil | ExxonMobil Method |
| Coating Weight | 25.0 g/m² | 15.6 lb/ream | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 190 % | 190 % | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Elongation at Break, TD | 55 % | 55 % | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Modulus of Elasticity | 1.70 GPa | 247 ksi | MD; ExxonMobil Method |
| 2.80 GPa | 406 ksi | TD; ExxonMobil Method | |
| Coefficient of Friction | 0.60 | 0.60 | Untreated Surface; ExxonMobil Method |
| Film Tensile Strength at Break, MD | 125 MPa | 18100 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Tensile Strength at Break, TD | 250 MPa | 36300 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 3.0 % @Temperature 135 °C, Time 432 sec |
3.0 % @Temperature 275 °F, Time 0.120 hour |
ExxonMobil Method |
| Shrinkage, TD | 3.0 % @Temperature 135 °C, Time 432 sec |
3.0 % @Temperature 275 °F, Time 0.120 hour |
ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 70 % | 70 % | 45°; ExxonMobil Method |
| Transmission, Visible | 32 % | 32 % | ExxonMobil Method |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Whiteness Index | 90 | |
| Yield | 27700 in2/lb |
Users viewing this material also viewed the following:
- Radici Radilon® A RV300RKC (cond.) Nylon 66
- Styron CALIBREâ„¢ 300EP 22 Polycarbonate, General Purpose
- SABIC Innovative Plastics LNP THERMOCOMP RC008 PA 66
- Unifrax FyreWrap® Cable Insulation
- A. Schulman ComAlloy® E-14292 Hi-Flow Glass Reinforced PPS
- ConocoPhillips Trolley Wire Lube
- ExxonMobil Label-Lyte® 90 LP Coated, High Sheen, Metallized, White Opaque OPP for Water-based Patch Label Applications
- BASF 1,4-Dioxane stab
- Buckeye Polymers BP RPP 2008 T NAT Polypropylene, Talc Filled
Copyright © lookpolymers.com All Rights Reserved