ExxonMobil Oppalyte™ 42MH647 OPP Film

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade
Manufacturer Exxon Chemical
Trade Name Oppalyte™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Oppalyte™ 42MH647 OPP Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: A super white opaque, modified higher density, biaxially oriented polypropylene film, acrylic coated two sides. It provides outstanding performance on all packaging machines.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features: Low sealing thresholdHigh seal strengths even under low pressure sealingGood aroma barrierExcellent packaging machine performanceOutstanding opacity, white background and reduced show-throughExcellent stiffnessIdeal support for normal ink systemsWater based coatingsFeatures:Acrylic CoatedFlavor & Aroma Barrier Light BarrierApplications:BakeryBiscuits/Cookie/Crackers Box OverwrapConfectionery, ChocolateConfectionery, GumConfectionery, SugarCrisps and SnacksDry Foods and Beverage Powders Health and Beauty Care Household and Detergents Pet food Uses: Box Overwrap Flexible PackagingHFFS Flexible Packaging Pre-made Bags – Flexible PackagingVFFS Flexible PackagingProcessing Method: Cold Seal Adhesive, Solvent Flexographic Printing, Solvent Rotogravure Printing and Surface Print UnsupportedInformation provided by ExxonMobil
Physical Properties Metric English Comments
Water Vapor Transmission 0.807 g/m²/day

@Temperature 23.0 °C
0.0520 g/100 in²/day

@Temperature 73.4 °F
85% RH; ExxonMobil Method
4.04 g/m²/day

@Temperature 38.0 °C
0.260 g/100 in²/day

@Temperature 100 °F
90% RH; ExxonMobil Method
Oxygen Transmission Rate 745 cc/m²/day

@Temperature 23.0 °C
48.0 cc/100 in²/day

@Temperature 73.4 °F
0% RH; ExxonMobil Method
751 cc/m²/day

@Temperature 23.0 °C
48.4 cc/100 in²/day

@Temperature 73.4 °F
Wet, 75% RH; ExxonMobil Method
Thickness 43.2 microns
1.70 mil
ExxonMobil Method
Coating Weight 30.6 g/m²
19.1 lb/ream
ExxonMobil Method
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 170 %
170 %
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Elongation at Break, TD 55 %
55 %
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Modulus of Elasticity 1.70 GPa
247 ksi
MD; ExxonMobil Method
2.80 GPa
406 ksi
TD; ExxonMobil Method
Coefficient of Friction 0.25
0.25
Both Sides; ExxonMobil Method
Seal Strength 610 g/25 mm

@Pressure 0.276 MPa,
Temperature 130 °C
610 g/in

@Pressure 40.0 psi,
Temperature 266 °F
Otto Brugger, 0.5 sec; ExxonMobil Method
Film Tensile Strength at Break, MD 105 MPa
15200 psi
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Tensile Strength at Break, TD 185 MPa
26800 psi
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Thermal Properties Metric English Comments
Shrinkage, MD 5.0 %

@Temperature 135 °C,
Time 432 sec
5.0 %

@Temperature 275 °F,
Time 0.120 hour
ExxonMobil Method
Shrinkage, TD 3.0 %

@Temperature 135 °C,
Time 432 sec
3.0 %

@Temperature 275 °F,
Time 0.120 hour
ExxonMobil Method
Optical Properties Metric English Comments
Gloss 70 %
70 %
45°; ExxonMobil Method
Transmission, Visible 25 %
25 %
ExxonMobil Method
Descriptive Properties Value Comments
Whiteness Index 70
Yield 22600 in2/lb