ExxonMobil Oppalyte™ 40MH247 OPP Film
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade |
| Manufacturer | Exxon Chemical |
| Trade Name | Oppalyte™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Oppalyte™ 40MH247 OPP Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: A super white opaque, modified higher density, biaxially oriented polypropylene film. This opaque and stiff film is ideal for mono material requirements and it has been especially designed for cold seal applications.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features: Excellent stiffness and flex resistanceOutstanding opacity, white background and reduced show-throughGood moisture barrierExceptional printability and receptivity to coatingsExcellent support for cold seal adhesionFeatures:Light BarrierApplications:BakeryBiscuits/Cookie/Crackers Confectionery, ChocolateConfectionery, GumConfectionery, SugarCrisps and SnacksDry Foods and Beverage Powders Frozen FoodHousehold and DetergentsIce Cream Uses: HFFS Flexible Packaging Processing Method: Cold Seal Adhesive, Inner Web Adhesive Lamination, Inner Web Extrusion Lamination, Outer Web Adhesive Lamination, Solvent Flexographic Printing, Solvent Rotogravure Printing and Surface Print UnsupportedInformation provided by ExxonMobil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Vapor Transmission | 0.900 g/m²/day @Temperature 23.0 °C |
0.0580 g/100 in²/day @Temperature 73.4 °F |
85% RH; ExxonMobil Method |
| 4.19 g/m²/day @Temperature 38.0 °C |
0.270 g/100 in²/day @Temperature 100 °F |
90% RH; ExxonMobil Method | |
| Thickness | 40.6 microns | 1.60 mil | ExxonMobil Method |
| Coating Weight | 28.5 g/m² | 17.8 lb/ream | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 170 % | 170 % | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Elongation at Break, TD | 55 % | 55 % | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Modulus of Elasticity | 1.70 GPa | 247 ksi | MD; ExxonMobil Method |
| 2.80 GPa | 406 ksi | TD; ExxonMobil Method | |
| Coefficient of Friction | 0.60 | 0.60 | Untreated Surface; ExxonMobil Method |
| Film Tensile Strength at Break, MD | 105 MPa | 15200 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Tensile Strength at Break, TD | 185 MPa | 26800 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 3.0 % @Temperature 135 °C, Time 432 sec |
3.0 % @Temperature 275 °F, Time 0.120 hour |
ExxonMobil Method |
| Shrinkage, TD | 3.0 % @Temperature 135 °C, Time 432 sec |
3.0 % @Temperature 275 °F, Time 0.120 hour |
ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 70 % | 70 % | 45°; ExxonMobil Method |
| Transmission, Visible | 25 % | 25 % | ExxonMobil Method |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Whiteness Index | 90 | |
| Yield | 24200 in2/lb |
Users viewing this material also viewed the following:
- Ferro EG 2770 Specialty Glass
- H.C. Starck Amperweld® AISI 316 L 150/53 µm for Plasma Transferred Arc Surfacing
- Shakespeare LMX-3 Easy Casting Nylon Copolymer Fishing Line, 15 lb
- Solvay Specialty Polymers Ryton® BR111BL Polyphenylene Sulfide (PPS), GlassMineral Filled
- Hexcel® HexPly® F655 Bismaleimide Resin, Carbon Fabric Form
- DSM Arnite® TV4 261 SF PBT-GF30 FR(17)
- ExxonMobil LDPE LD 259 Low Density Polyethylene Resin (European Grade)
- Covestro Bayflex® MP-10000 Polyurethane Elastomeric RIM, MDI-based 2-Component Liquid System
- Arkema Group Orgalloy® RS 6010 Polyamide 6 Alloy 10% Glass Fiber reinforced
Copyright © lookpolymers.com All Rights Reserved