ExxonMobil Oppalyte™ 50MH247 OPP Film
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade |
| Manufacturer | Exxon Chemical |
| Trade Name | Oppalyte™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Oppalyte™ 50MH247 OPP Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: A super white opaque, modified higher density, biaxially oriented polypropylene film. This opaque and stiff film is ideal for mono material requirements and it has been especially designed for cold seal applications.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features:Excellent stiffness and flex resistance Outstanding opacity, white background and reduced show-throughGood moisture barrierExceptional printability and receptivity to coatingsExcellent support for cold seal Features: Light BarrierApplications:BakeryBiscuits/Cookie/Crackers Confectionery, ChocolateConfectionery, GumConfectionery, SugarCrisps and SnacksDry Foods and Beverage Powders Frozen Food Household and Detergents Ice Cream Uses:HFFS Flexible Packaging Processing Method: Cold Seal Adhesive, Inner Web Adhesive Lamination, Inner Web Extrusion Lamination, Outer Web Adhesive Lamination, Solvent Flexographic Printing, Solvent Rotogravure Printing and Surface Print UnsupportedInformation provided by ExxonMobil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Vapor Transmission | 0.497 g/m²/day @Temperature 23.0 °C |
0.0320 g/100 in²/day @Temperature 73.4 °F |
85% RH; ExxonMobil Method |
| 2.95 g/m²/day @Temperature 38.0 °C |
0.190 g/100 in²/day @Temperature 100 °F |
90% RH; ExxonMobil Method | |
| Thickness | 50.8 microns | 2.00 mil | ExxonMobil Method |
| Coating Weight | 35.7 g/m² | 22.3 lb/ream | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 170 % | 170 % | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Elongation at Break, TD | 55 % | 55 % | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Modulus of Elasticity | 1.70 GPa | 247 ksi | MD; ExxonMobil Method |
| 2.80 GPa | 406 ksi | TD; ExxonMobil Method | |
| Coefficient of Friction | 0.60 | 0.60 | Untreated Surface; ExxonMobil Method |
| Film Tensile Strength at Break, MD | 105 MPa | 15200 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Tensile Strength at Break, TD | 185 MPa | 26800 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 3.0 % @Temperature 135 °C, Time 432 sec |
3.0 % @Temperature 275 °F, Time 0.120 hour |
ExxonMobil Method |
| Shrinkage, TD | 3.0 % @Temperature 135 °C, Time 432 sec |
3.0 % @Temperature 275 °F, Time 0.120 hour |
ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 70 % | 70 % | 45°; ExxonMobil Method |
| Transmission, Visible | 22 % | 22 % | ExxonMobil Method |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Whiteness Index | 90 | |
| Yield | 19300 in2/lb |
Users viewing this material also viewed the following:
- MV Labs K910 K2HPO4 Potassium hydrogen phosphate
- RheTech Products F56-01 40% Glass Fiber/Mineral Co-Reinforced Polypropylene, Chemically Coupled, Black
- SABIC Innovative Plastics Lexan® 955A PC
- Gwent Electronic Materials D2070423D5 Polymer Dielectric
- A. Schulman POLYBATCH™ White LL8425 MG Concentrate Based In LLDPE
- DuPont Teijin Films Mylar® P25 Polyester Film, 50 Gauge
- Arlon 30400N060 0.060" (1.52 mm) Uncured Silicone Rubber
- BASF Formic Acid - 90%
- Teknor Apex APEX® 3075-H Polyvinyl Chloride, Flexible
Copyright © lookpolymers.com All Rights Reserved