Techmer ES HiFill® POM HO UV
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Unreinforced |
| Manufacturer | Techmer ES |
| Trade Name | HiFill® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES HiFill® POM HO UV.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsAdditive: UV StabilizerFeatures: HomopolymerInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ASTM D792 |
| Water Absorption | 0.15 % @Time 86400 sec |
0.15 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.018 cm/cm @Thickness 3.17 mm |
0.018 in/in @Thickness 0.125 in |
ASTM D955 |
| Melt Flow | 7.0 g/10 min @Load 1.05 kg, Temperature 190 °C |
7.0 g/10 min @Load 2.31 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength, Yield | 64.1 MPa | 9300 psi | ASTM D638 |
| Elongation at Break | 12 % | 12 % | ASTM D638 |
| Flexural Yield Strength | 82.7 MPa | 12000 psi | ASTM D790 |
| Flexural Modulus | 3.24 GPa | 470 ksi | ASTM D790 |
| Izod Impact, Notched | 0.801 J/cm @Thickness 3.17 mm |
1.50 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 90.0 µm/m-°C | 50.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 334 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C | 219 °F | Unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Nye Lubricants UniFlor 8512G (842G) (UF) Synthetic Oil
- Solvay Specialty Polymers Primef® 7002 Polyphenylene Sulfide (PPS), 65% GlassMineral (discontinued **)
- Kennametal Stellite Stellite® 238 Cobalt Alloy
- Techmer ES HiFill® PA4/6 GF50 HS BK 50% Glass Filled
- A. Schulman POLYBATCH™ White B8750A Concentrate Based In HDPE
- DuPont Teijin Films Mylar® M461 Polyester Film, 75 Gauge
- Arlon 56811B025 0.026" (0.660 mm) Uncured Silicone Rubber with Fiberglass Substrate
- Abatron AboCast 37-10/AboCure 37-10 Adhesive/Casting
- Braskem H 401 Cast Film Extrusion Polypropylene
Copyright © lookpolymers.com All Rights Reserved