Entec Hylex® P1307L1 HB Polycarbonate
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Optical Grade |
| Manufacturer | Entec Engineered Resins |
| Trade Name | Hylex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Entec Hylex® P1307L1 HB Polycarbonate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
UV Stabilized, Low Flow, Mold Release, Water ClearInformation provided by Entec.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ASTM D792 |
| Water Absorption at Saturation | 0.15 % | 0.15 % | Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.005 - 0.007 cm/cm | 0.005 - 0.007 in/in | ASTM D955 |
| Melt Flow | 7.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
7.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D638 |
| Elongation at Break | 130 % | 130 % | ASTM D638 |
| Flexural Strength | 93.1 MPa | 13500 psi | ASTM D790 |
| Flexural Modulus | 2.41 GPa | 350 ksi | ASTM D790 |
| Izod Impact, Notched | 8.54 J/cm | 16.0 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 124 °C | 255 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
|
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.586 | 1.586 | ASTM D542 |
| Haze | 1.0 % | 1.0 % | ASTM D1003 |
| Transmission, Visible | 88 % | 88 % | ASTM D1003 |
Users viewing this material also viewed the following:
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer with 6 PHR Di-Cup 40C
- Flint Hills P5M5R-083 Random Copolymer Polypropylene
- Solvay TECHNYL® B 50 H1 PA66/6, DRY
- Solvay TECHNYL® CR 218 V33 Black 21 N Nylon 6, 30% glass fiber, DRY
- SABIC Innovative Plastics LNP THERMOCOMP PFW53U PA 6 (Asia Pacific)
- ExxonMobil PP1064L1 Polypropylene Homopolymer
- Arlon CLTE-P Pre-Preg Bonding Layer
- Ashley Polymers Ashlene® 528L-40G Nylon 66, 40% Glass Reinforced
- Arkema Group Rilsan® AZM 50 NOIR T6LD Nylon 12, 50% Glass Fiber Filled (Conditioned)
Copyright © lookpolymers.com All Rights Reserved