Arkema Group Pebax® 5533 Polyether Block Amide (PEBA)
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyether Block Amide (PEBA) |
| Manufacturer | Arkema |
| Trade Name | Pebax® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arkema Group Pebax® 5533 Polyether Block Amide (PEBA).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Arkema Group
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.01 g/cc | 0.0365 lb/in³ | ASTM D792 |
| Water Absorption | 1.2 % | 1.2 % | 24 hr in water at 20°C; ASTM D570 |
| Water Absorption at Saturation | 0.50 % | 0.50 % | 20°C and 65% RH; ASTM D570 |
| Melt Flow | 7.0 g/10 min | 7.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 55 | 55 | ASTM D2240 |
| Tensile Strength at Break | 44.0 MPa | 6380 psi | ASTM D638 |
| Tensile Strength, Yield | 12.0 MPa | 1740 psi | ASTM D638 |
| Elongation at Break | 500 % | 500 % | ASTM D638 |
| Elongation at Yield | 25 % | 25 % | ASTM D638 |
| Modulus of Elasticity | 0.145 GPa | 21.0 ksi | ASTM D638 |
| Flexural Modulus | 0.160 GPa | 23.2 ksi | ASTM D790 |
| Resilience | 0.585 | 0.585 | BS 903 par: A 8 |
| Flex Crack Resistance | 3.0 | 3.0 | [mm] 20°C / 100000 flexures; ASTM D813 |
| 9.0 | 9.0 | [mm] -20°C / 50000 flexures; ASTM D813 | |
| Izod Impact, Notched | NB | NB | ASTM D256-A |
| NB @Temperature -40.0 °C |
NB @Temperature -40.0 °F |
ASTM D256-A | |
| Izod Impact, Unnotched | NB | NB | ASTM D256-A |
| NB @Temperature -40.0 °C |
NB @Temperature -40.0 °F |
ASTM D256-A | |
| Tear Strength | 115 kN/m | 656 pli | notched; ASTM D624 (C) |
| 135 kN/m | 770 pli | unnotched; ASTM D624 (C) | |
| Taber Abrasion, mg/1000 Cycles | 65 | 65 | ASTM D1242 |
| Abrasion | 50 | 50 | mm<sup>3</sup>; DIN 53516 |
| Compression Set | 10 % | 10 % | Load = 9.3 MPa (22 hr / 70°C); ASTM D395 Method A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Heat of Fusion | 26.0 J/g | 11.2 BTU/lb | ASTM D3417 |
| CTE, linear | 170 µm/m-°C @Temperature -40.0 - 140 °C |
94.4 µin/in-°F @Temperature -40.0 - 284 °F |
ASTM D696 |
| Melting Point | 159 °C | 318 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 66.0 °C | 151 °F | ASTM D648 |
| Vicat Softening Point | 144 °C | 291 °F | under 1 daN; ASTM D1525 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 3.00e+12 ohm @Temperature 20.0 °C |
3.00e+12 ohm @Temperature 68.0 °F |
65% RH; ASTM D257 |
Users viewing this material also viewed the following:
- Quadrant EPP Ketron® CA30 PEEK + carbon fibres, extruded (ISO Data)
- Resin Technology Group CT-988 Cationic UV Cure Epoxy Adhesive
- Polimeri Europa KOBLEND HI 20 PBT+PC, Impact Grade (discontinued **)
- Solvay TECHNYL® A 303 Natural FA PA66, Conditioned
- Elektro-Isola Etronit IS Phenolic, Paper Reinforcement, Dark Brown, Sheets
- DuPont Teijin Films Mylar® M34 Polyester Film, 75 Gauge (20 µm), PVDC Coated
- BASF Ultramid® B3EG3 BK 00564 15% Glass Filled PA6 (Conditioned)
- 3A Composites Core Materials AIREX® PXc.385 Fiber-Reinforced Structural Foam
- Teknor Apex Sinvicomp SBB 3615 Polyvinyl Chloride, Rigid
- Vyncolit INSUL-PLATE™ X-28057-2HT Hole-Fill Powder For Printed Circuit Boards
Copyright © lookpolymers.com All Rights Reserved