- Eurostar Starpylen MZ006S PP, Glass Fiber Filled, Injection Molded
Eurostar Starpylen MZ006S PP, Glass Fiber Filled, Injection Molded
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Starpylen |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Starpylen MZ006S PP, Glass Fiber Filled, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Starpylen MZ006S is a Glass fiber Reinforced, Polypropylene Injection Molding Resin heat stabilized (also known as Starpylen WT 30GF S3)Information provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0060 cm/cm @Thickness 4.00 mm |
0.0030 - 0.0060 in/in @Thickness 0.157 in |
E2P method |
| Melt Flow | 5.0 - 10 g/10 min @Load 5.00 kg, Temperature 230 °C |
5.0 - 10 g/10 min @Load 11.0 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 35.0 MPa | 5080 psi | 5 mm/min; ISO 527 |
| Elongation at Yield | 5.0 - 7.0 % | 5.0 - 7.0 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 4.20 GPa | 609 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 65.0 MPa | 9430 psi | 2 mm/min; ISO 178 |
| Flexural Yield Strength | 45.0 MPa | 6530 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 3.00 GPa | 435 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 20.0 kJ/m² | 9.52 ft-lb/in² | 80x10x4; ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 136 °C | 277 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 195 - 205 °C | 383 - 401 °F | |
| Zone 2 | 215 - 225 °C | 419 - 437 °F | |
| Zone 3 | 225 - 250 °C | 437 - 482 °F | |
| Melt Temperature | 225 - 250 °C | 437 - 482 °F | |
| Mold Temperature | 40.0 - 70.0 °C | 104 - 158 °F |
Users viewing this material also viewed the following:
- MV Labs PD430 (NH4)2PdCl6 Ammonium hexachloropalladate(IV)
- SABIC Innovative Plastics EXTEM VH1003F PEI Copolymer (Europe-Africa-Middle East)
- Polymer Resources NY6-G13-[color]-H Nylon 6, 13% Glass Reinforced, Heat Stabilized
- Parker Chomerics CHO-BOND 2165 Polyurethane Sealant
- Teknor Apex APEX® 3301-50 Polyvinyl Chloride, Flexible
- Suqian Unitechem Light Stabilizer 944
- BASF Polystyrol® 432 B Impact Grade Polystyrene (Europe)
- Azoty Tarnow™ Tarnamid® T-27 MCS Polyamide 6 - Colored
- AorTech Biomaterials Elast-Eon™ E5-325 Biomedical Polyurethane Pellets
- Ineos Nova 5490 High Impact Polystyrene (discontinued **)
Copyright © lookpolymers.com All Rights Reserved