- Polymer Property : Melt Flow = 10 g/10 min
Polymer Property : Melt Flow = 10 g/10 min Product List
Physical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 2.0 - 10 g/10 min @Load 2.16 kg, Temperature 265 °C |
2.0 - 10 g/10 min @Load 4.76 lb, Temperature 509 °F |
ASTM D1238 |
| Polymer Resources PC/TP-GP2-G10 PC/Polyester Alloy, 10% Glass Reinforced Excellent Chemical Resistance, 10% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information p.. |
|||
| Melt Flow | 5.0 - 10 g/10 min @Load 2.16 kg, Temperature 265 °C |
5.0 - 10 g/10 min @Load 4.76 lb, Temperature 509 °F |
ASTM D1238 |
| Polymer Resources PC/TP-GP2-G20 PC/Polyester Alloy, 20% Glass Reinforced Excellent Chemical Resistance, 20% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information p.. |
|||
| Melt Flow | 5.0 - 10 g/10 min @Load 1.20 kg, Temperature 300 °C |
5.0 - 10 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Polymer Resources PC-GP1-D-[color]-1 Polycarbonate, General Purpose, Low Flow with Mold Release Polycarbonate, General Purpose, Low Flow with Mold ReleaseProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Inform.. |
|||
| Melt Flow | 5.0 - 10 g/10 min @Load 2.16 kg, Temperature 250 °C |
5.0 - 10 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Polymer Resources TP-G40 Polybutylene Terephthalate, 40% Glass Reinforced Polybutylene Terephthalate, 40% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information prov.. |
|||
| Melt Flow | 1.0 - 10 g/10 min @Load 5.00 kg, Temperature 250 °C |
1.0 - 10 g/10 min @Load 11.0 lb, Temperature 482 °F |
ASTM D1238 |
| Polymer Resources PC/ABS-G40 General Purpose PC/ABS Alloy, 40% Glass Filled PC/ABS Alloy, General Purpose, 40% Glass FilledProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provi.. |
|||
| Melt Flow | 5.0 - 10 g/10 min @Load 5.00 kg, Temperature 200 °C |
5.0 - 10 g/10 min @Load 11.0 lb, Temperature 392 °F |
ISO 1133 |
| Ineos Nova 602 Crystal Polystyrene GP Grade
(discontinued **) Broad, medium melt flow range, Broad Vicat rangeApplications: Any; Injection Molding and ExtrusionProperties were determined on injection molded specimens at 23°C and 50% R.H. unless otherwise spe.. |
|||
| Melt Flow | 7.0 - 10 g/10 min | 7.0 - 10 g/10 min | ASTM D1238 |
| Kolon KOCETAL® LF302 Wear Modified Acetal Resin Improved wear property and dimensional stability. Applications: Products for low noise and precision gear. Information provided by API-Kolon. |
|||
| Melt Flow | 8.0 - 10 g/10 min | 8.0 - 10 g/10 min | ASTM D1238 |
| Micropol Microlin ML21 Linear Polyethylene Rotational Molding Powder Information provided by Micropol Limited |
|||
| Melt Flow | 2.0 - 10 g/10 min | 2.0 - 10 g/10 min | (Condition L) ASTM D-1238 |
| Multibase Multi-Flex® TPE A 4710 NAT The burn rate is 1 in/min (25 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
| Melt Flow | 6.0 - 10 g/10 min @Temperature 230 °C |
6.0 - 10 g/10 min @Temperature 446 °F |
ASTM D1238 |
| A. Schulman PP 1259 Polypropylene Medium Impact Polypropylene DescriptionPolypropylene PP 1259 is a medium impact polypropylene with easier molding characteristics for thinner parts and longer flow distances. Lower molding pressures and heats often reduce war.. |
|||
| Melt Flow | 5.0 - 10 g/10 min | 5.0 - 10 g/10 min | 230/2.16; May be specified; ASTM D1238 |
| Plastics Group Polifil® GFPPCC-40 40% Glass Reinforced Polypropylene Polifil® GFPPCC series compounds are homopolymer polypropylenes reinforced with chemically coupled glass fibers. These compounds offer superior strength and stiffness, improved elevated temperature.. |
|||
| Melt Flow | 5.0 - 10 g/10 min | 5.0 - 10 g/10 min | 230/2.16; May be specified; ASTM D1238 |
| Plastics Group Polifil® GFRMPPCC-30 30% Glass Reinforced Polypropylene, High Impact Polifil® GFRMPPCC series compounds are high impact polypropylenes reinforced with chemically coupled glass fibers. This combination provides higher impact strength while retaining high stiffness.Ap.. |
|||
| Melt Flow | 6.0 - 10 g/10 min @Temperature 230 °C |
6.0 - 10 g/10 min @Temperature 446 °F |
ASTM D1238 |
| A. Schulman PP 1259 Polypropylene Medium Impact Polypropylene DescriptionPolypropylene PP 1259 is a medium impact polypropylene with easier molding characteristics for thinner parts and longer flow distances. Lower molding pressures and heats often reduce war.. |
|||
| Melt Flow | 5.0 - 10 g/10 min @Temperature 230 °C |
5.0 - 10 g/10 min @Temperature 446 °F |
Condition L; ASTM D1238 |
| A. Schulman POLYFORT™ FPP 1285 Glass Fiber-Reinforced Copolymer Polypropylene DescriptionPolyfort® FPP1285 is a 20% glass fiber-reinforced copolymer polypropylene.Information provided by A. Schulman. |
|||
| Melt Flow | 7.0 - 10 g/10 min @Temperature 230 °C |
7.0 - 10 g/10 min @Temperature 446 °F |
ASTM D1238 |
| A. Schulman POLYFORT™ FPP 2122UV-M-31 Black, Talc Filled Copolymer Polypropylene DescriptionPolyfort® FPP 2122UV-M-31 is a black 40% talc filled polypropylene. It is weather and urethane contact resistant and contains a mold release. Information provided by A. Schulman. |
|||
| Melt Flow | 7.0 - 10 g/10 min @Temperature 230 °C |
7.0 - 10 g/10 min @Temperature 446 °F |
Condition L; ASTM D1238 |
| A. Schulman POLYFORT™ FPP 2388 Glass Reinforced Polypropylene DescriptionPolyfort® FPP 2388 is a 5% glass reinforced polypropylene.Information provided by A. Schulman. |
|||
| Melt Flow | 7.0 - 10 g/10 min @Temperature 230 °C |
7.0 - 10 g/10 min @Temperature 446 °F |
ASTM D1238 |
| A. Schulman POLYFORT™ FPP 2122UV-M-31 Black, Talc Filled Copolymer Polypropylene DescriptionPolyfort® FPP 2122UV-M-31 is a black 40% talc filled polypropylene. It is weather and urethane contact resistant and contains a mold release. Information provided by A. Schulman. |
|||
| Melt Flow | 6.0 - 10 g/10 min @Temperature 230 °C |
6.0 - 10 g/10 min @Temperature 446 °F |
ASTM D1238 |
| A. Schulman PP 1259 Polypropylene Medium Impact Polypropylene DescriptionPolypropylene PP 1259 is a medium impact polypropylene with easier molding characteristics for thinner parts and longer flow distances. Lower molding pressures and heats often reduce war.. |
|||
| Melt Flow | 5.0 - 10 g/10 min | 5.0 - 10 g/10 min | 230/2.16; May be specified; ASTM D1238 |
| Plastics Group Polifil® GFPPCC-20 20% Glass Reinforced Polypropylene Polifil® GFPPCC series compounds are homopolymer polypropylenes reinforced with chemically coupled glass fibers. These compounds offer superior strength and stiffness, improved elevated temperature.. |
|||
| Melt Flow | 5.0 - 10 g/10 min | 5.0 - 10 g/10 min | 230/2.16; May be specified; ASTM D1238 |
| Plastics Group Polifil® GFRMPPCC-20 20% Glass Reinforced Polypropylene, High Impact Polifil® GFRMPPCC series compounds are high impact polypropylenes reinforced with chemically coupled glass fibers. This combination provides higher impact strength while retaining high stiffness.Ap.. |
|||
| Melt Flow | 5.0 - 10 g/10 min | 5.0 - 10 g/10 min | ASTM D1238 |
| A. Schulman POLYFORT™ FPP 1182 Talc Fortified Impact Resistant Polypropylene DescriptionPolyfort® FPP 1182 is a 20% talc fortified impact resistant polypropylene.Information provided by A. Schulman. |
|||
| Melt Flow | 5.0 - 10 g/10 min | 5.0 - 10 g/10 min | ISO 1133 |
| Chengdu Polyster FH2040 Thermoplastic Polyether-ester Elastomer (TPEE) Blend of H2040 and self-made flame retardant material. Excellent flex resistance at low temperatures. Excellent flex-fatigue resistance. Applications requiring flexibility at low temperatures and fl.. |
|||
| Melt Flow | 4.0 - 10 g/10 min @Load 5.00 kg, Temperature 372 °C |
4.0 - 10 g/10 min @Load 11.0 lb, Temperature 702 °F |
|
| Daikin NEOFLON NP-120 FEP Pellets NEOFLON FEP molding materials are supplied as translucent white pellets for melt flow processes.Processing Methods: Extrusion molding.Applications: Heavy wall wire insulation, cable jacketing, tubes.. |
|||
| Melt Flow | 5.0 - 10 g/10 min @Load 5.00 kg, Temperature 230 °C |
5.0 - 10 g/10 min @Load 11.0 lb, Temperature 446 °F |
ISO 1133 |
| Eurostar Starpylen MZ006S PP, Glass Fiber Filled, Injection Molded Starpylen MZ006S is a Glass fiber Reinforced, Polypropylene Injection Molding Resin heat stabilized (also known as Starpylen WT 30GF S3)Information provided by Eurostar. |
|||
| Melt Flow | 6.0 - 10 g/10 min | 6.0 - 10 g/10 min | ASTM D1238 |
| Buckeye Polymers BP HDPE 9610 R RLK High Density Polyethylene Product Information: Our HDPE grade of materials are designed to offer excellent physical properties while providing cost savings versus higher cost prime equivalents. Buckeye Polymers HDPE materia.. |
|||
| Melt Flow | 6.0 - 10 g/10 min | 6.0 - 10 g/10 min | ASTM D1238 |
| Buckeye Polymers BP RPP 2008 T NAT Polypropylene, Talc Filled Product Information: Our Talc filled product lines exhibit excellent properties such as high stiffness, surface aesthetics, low coefficient of thermal expansion, low shrinkage, improved scratch and .. |
|||
| Melt Flow | 5.0 - 10 g/10 min | 5.0 - 10 g/10 min | ASTM D1238 |
| Aaron Industries AAROPRENE® GFABS 4020 Glass Filled Acrylonitrile-Butadiene Styrene AAROPRENE® GFABS 4000 Series Reinforced CompoundsMelt flow index may be specified. Color may be specified. |
|||
| Melt Flow | 8.0 - 10 g/10 min | 8.0 - 10 g/10 min | 230/3.8, nominal; ASTM D1238 |
| Plastics Group Polifil® RP-ABS Acrylonitrile-Butadiene Styrene, High Flow Version Polifil® RP- Acrylonitrile-Butadiene Styrene is a styrenic resin with improved toughness and heat resistance versus HIPS grades. ABS exhibits high gloss, low shrinkage, and good dimensional stabili.. |
|||
| Melt Flow | 7.0 - 10 g/10 min @Load 12.5 kg |
7.0 - 10 g/10 min @Load 27.6 lb |
|
| Solvay Specialty Polymers Hylar® MP20 PVDF Polyvinylidene Fluoride
(discontinued **) Data provided by the manufacturer.Hylar® polymers have the characteristic stability of fluoropolymers combined with a unique polarity that influences its solubility and electrical properties. In a.. |
|||
| Melt Flow | 8.0 - 10 g/10 min | 8.0 - 10 g/10 min | |
| Ashley Polymers Ashlene® R190H Acetal General purpose, reprocessed copolymer, excellent toughness, strength, stiffness and lubricity. UV stabilized for good weatherability. Available in Natural and Black. Natural: Designated R190H-N3.. |
|||