Plastics Group Polifil® GFPPCC-20 20% Glass Reinforced Polypropylene

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Glass Fiber Filler
Manufacturer The Plastics Group of America
Trade Name Polifil®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Plastics Group Polifil® GFPPCC-20 20% Glass Reinforced Polypropylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polifil® GFPPCC series compounds are homopolymer polypropylenes reinforced with chemically coupled glass fibers. These compounds offer superior strength and stiffness, improved elevated temperature performance, better creep resistance, higher impact strength and higher resistance to high temperature water than conventional glass fiber reinforced polypropylenes.Applications: Chemical resistanceAppliancesElectrical componentsAutomotiveIrrigationUtility productsStandard processing techniques are applicable. Information provided by The Plastics Group.
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
ASTM D792
Filler Content 20 %
20 %
ASTM D2584
Linear Mold Shrinkage 0.0040 cm/cm

@Thickness 1.59 mm
0.0040 in/in

@Thickness 0.0625 in
ASTM D955
Melt Flow 5.0 - 10 g/10 min
5.0 - 10 g/10 min
230/2.16; May be specified; ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 81.4 MPa
11800 psi
ASTM D638
Elongation at Break 4.0 %
4.0 %
ASTM D638
Flexural Strength 93.1 MPa
13500 psi
ASTM D638
Flexural Modulus 3.52 GPa
510 ksi
Tangent; ASTM D790
Izod Impact, Notched 0.908 J/cm
1.70 ft-lb/in
At 73°F; ASTM D256
Gardner Impact 0.678 J
0.500 ft-lb
ASTM D3029
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 151 °C
303 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 138 °C
280 °F
ASTM D648