Solvay Specialty Polymers Hylar® MP20 PVDF Polyvinylidene Fluoride  (discontinued **)

Category Polymer , Thermoplastic , Fluoropolymer , PVDF , Polyvinylidinefluoride (PVDF), Molded/Extruded
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Hylar® MP20 PVDF Polyvinylidene Fluoride  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by the manufacturer.Hylar® polymers have the characteristic stability of fluoropolymers combined with a unique polarity that influences its solubility and electrical properties. In addition to standard molding and extrusion, Hylar® polymers lend themselves well to solution-applied coatings.
Physical Properties Metric English Comments
Density 1.77 - 1.79 g/cc
0.0639 - 0.0647 lb/in³
ASTM D792
Water Absorption 0.020 %
0.020 %
ASTM D570
Linear Mold Shrinkage 0.025 - 0.030 cm/cm
0.025 - 0.030 in/in
Melt Flow 7.0 - 10 g/10 min

@Load 12.5 kg
7.0 - 10 g/10 min

@Load 27.6 lb
Mechanical Properties Metric English Comments
Hardness, Shore D 76 - 80
76 - 80
ASTM D2240
Tensile Strength, Ultimate 35.0 - 45.0 MPa
5080 - 6530 psi
ASTM D638
Tensile Strength, Yield 35.0 - 48.0 MPa
5080 - 6960 psi
ASTM D638
Elongation at Break 50 - 250 %
50 - 250 %
ASTM D638
Elongation at Yield 10 %
10 %
ASTM D638
Tensile Modulus 1.38 - 1.73 GPa
200 - 251 ksi
ASTM D638
Flexural Yield Strength 48.0 - 55.0 MPa
6960 - 7980 psi
ASTM D790
Flexural Modulus 1.138 - 2.07 GPa
165.1 - 300 ksi
ASTM D790
Izod Impact, Notched 0.800 - 1.30 J/cm
1.50 - 2.44 ft-lb/in
Izod Impact, Unnotched NB
NB
Low Temp; ASTM D256
Coefficient of Friction, Dynamic 0.10 - 0.25
0.10 - 0.25
ASTM D1894
Coefficient of Friction, Static 0.15
0.15
ASTM D1894
Thermal Properties Metric English Comments
CTE, linear 100 - 120 µm/m-°C

@Temperature 20.0 °C
55.6 - 66.7 µin/in-°F

@Temperature 68.0 °F
ASTM D696
Specific Heat Capacity 1.90 J/g-°C
0.454 BTU/lb-°F
DSC
Thermal Conductivity 0.190 - 0.220 W/m-K
1.32 - 1.53 BTU-in/hr-ft²-°F
ASTM C177
Melting Point 165 - 168 °C
329 - 334 °F
ASTM D3418
Maximum Service Temperature, Air 150 °C
302 °F
No oxidative or thermal degradation after 5 years at 150°C (300°F)
Deflection Temperature at 1.8 MPa (264 psi) 105 - 115 °C
221 - 239 °F
TMA
Brittleness Temperature <= -43.0 °C
<= -45.4 °F
ASTM D2236
Flammability, UL94 V-0
V-0
Oxygen Index 43 %
43 %
ASTM D2863
Optical Properties Metric English Comments
Refractive Index 1.42
1.42
Electrical Properties Metric English Comments
Electrical Resistivity 1.40e+16 ohm-cm
1.40e+16 ohm-cm
ASTM D257
Dielectric Constant 6.0

@Frequency 1e+6 Hz
6.0

@Frequency 1e+6 Hz
ASTM D150
6.8

@Frequency 60 Hz
6.8

@Frequency 60 Hz
ASTM D150
Dielectric Strength 12.4 kV/mm

@Thickness 3.17 mm
315 kV/in

@Thickness 0.125 in
Short-Time 500 V/sec
Dissipation Factor 0.032

@Frequency 60 Hz
0.032

@Frequency 60 Hz
ASTM D150
0.153

@Frequency 1e+6 Hz
0.153

@Frequency 1e+6 Hz
ASTM D150
Arc Resistance >= 50 sec
>= 50 sec
ASTM D495
Processing Properties Metric English Comments
Processing Temperature 215 - 232 °C
419 - 450 °F
Preheat