- Polymer Property : Melt Flow = 2.0 g/10 min
Polymer Property : Melt Flow = 2.0 g/10 min Product List
Physical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | (Condition L) ASTM D-1238 |
| Multibase Multi-Flex® TPE D 4502 BLK Multi-Flex® D 4502 is based on Shell's Kraton G polymer and is suitable for applications for the automotive industry. It exhibits excellent paintability adhesion and is recommended as substrate fo.. |
|||
| Melt Flow | 2.0 g/10 min @Load 0.325 kg, Temperature 270 °C |
2.0 g/10 min @Load 0.716 lb, Temperature 518 °F |
|
| Plastcom SLOVAMID 6 GF 20 FRG 3 PA6, 20% glass fibre, flame retardant FeaturesPA 6 for injection moulding, chemically reinforced with 20 % glass fibre, with halogen free flame retardant. Main features: flammability in accordance with UL 94 V2 at 1.6 mm, glow wire at 9.. |
|||
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
|
| Plastcom SLOVAMID 6 GF 35 FRC 5 PA6 reinforced with 35% glass fibre, with flame retardant PA 6 for injection moulding, chemically reinforced with 35 % glass fibre, with halogen free flame retardant. Main features: flammability in accordance with UL 94 V2 at 1.6 mm, glow wire at 750°C, C.. |
|||
| Melt Flow | 2.0 - 7.0 g/10 min @Load 11.6 kg, Temperature 250 °C |
2.0 - 7.0 g/10 min @Load 25.6 lb, Temperature 482 °F |
ASTM D1238 |
| Polymer Resources PPX-GP5 Modified-PPO, General Purpose Modified-Polyphenylene Oxide, General Purpose, 270F HDTProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Informati.. |
|||
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | Exxon Method |
| ExxonMobil Escorene® LD-104 LDPE Packaging Film Resin, High Clarity
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A homopolymer packaging film resin with excellent clarity and good stiffness. It is excellent either blown film or chill roll casting equipment. I.. |
|||
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ASTM D1238 |
| Huntsman PE1044 Film Extrusion Polyethylene
(discontinued **) Homopolymer, and FDA compliant.Features: Yields film with excellent optical and machinability.Applications: Film extrusion: soft goods and other high clarity packaging.FDA Notes: Conforms to FDA reg.. |
|||
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ASTM D1238 |
| Huntsman PE1065 Film Extrusion Polyethylene
(discontinued **) Homopolymer and FDA compliant.Features: Yields film with excellent optical and machinability.Applications: Film extrusion: soft goods and other high clarity packaging.FDA Notes: Conforms to FDA regu.. |
|||
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | Exxon Method |
| ExxonMobil Escorene® LD-319 EVA Film Resin
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A 9.0% vinyl acetate copolymer film resin. Film made from LD-319 exhibits superior impact strength and heat sealability.Applications: Primal meat b.. |
|||
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
Condition L; ASTM D1238 |
| LyondellBasell Pro-faxâ„¢ SR257M Polypropylene Copolymer Description: Pro-faxâ„¢ SR257M clarified polypropylene random copolymer resin has excellent see-through and contact clarity. This resin offers source reduction potential in blow molding and extru.. |
|||
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ASTM D1238 |
| LyondellBasell Plexar® PX3236 Extrudable Tie-Layer Resin - Anhydride Modified LLDPE General DescriptionPLEXAR tie-layers are chemically modified resins used to bond unlike materials, primarily in packaging and industrial applications. Common adherents include polyethylene resins a.. |
|||
| Melt Flow | 2.0 - 3.0 g/10 min @Load 5.00 kg, Temperature 190 °C |
2.0 - 3.0 g/10 min @Load 11.0 lb, Temperature 374 °F |
ISO 1133 |
| FKuR Kunststoff Fibrolon® P 8540 Wood-Plastic Compound, Fiber Reinforced FIBROLON® are fiber reinforced compounds. Fibrolon® P 8540 has a polypropylene base. With the brand name of FIBROLON® FKuR has developed natural fiber reinforced compounds (Wood-Plastics-C.. |
|||
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ASTM D1238 |
| Flint Hills 23S1Acs256 Random Copolymer Polypropylene Features: High contact clarity, blush resistant, good impact and flexural modulus. Product does not contain animal derived components.Applications: Blow molded articles - Food, health, medical an.. |
|||
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Ineos H02G-02 Polypropylene Homopolymer This is a homopolymer designed for extrusion and film. It exhibits good extrusion and film orientation behavior. This material meets the requirements of the U.S. Food and Drug Administration as sp.. |
|||
| Melt Flow | 2.0 - 10 g/10 min | 2.0 - 10 g/10 min | (Condition L) ASTM D-1238 |
| Multibase Multi-Flex® TPE A 4710 BLK The burn rate is 1 in/min (25 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ISO 1133-1981E |
| LyondellBasell DP 8220M Polybutene Key Features: semi-crystalline, medium ethylene content random copolymer, reduces seal initiation temperature, FDA acceptableApplications: seal-peel layer of BOPP filmMeets FDA requirements in 21 CF.. |
|||
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 400 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 752 °F |
ASTM D1238 |
| Solvay Specialty Polymers AvaSpire® AV-621 GF30 Polyaryletherketone (PAEK), 30% Glass Fiber AvaSpire® AV-621 GF30 is a 30% glass fiber reinforced version of AvaSpire® AV-621. This formulation offers better dimensional stability and lower warpage than 30% glass reinforced PEEK. This r.. |
|||
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
Base Resin; ISO 1133 |
| Borealis Superclean™ LR4201S Crosslinkable Polyethylene Insulation for Medium and High Voltage Power Cables Superclean LR4201S is a Superclean crosslinkable low density polyethylene (XLPE) for medium and high voltage power cable insulation. The formulation of LR4201S provides an optimum combination of go.. |
|||
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ASTM D1238 |
| Westlake Mxsten CV77518 Polyethylene Plastomer Mxsten CV Plastomer CV77518 resin is a polyethylene plastomer designed for blown and cast film extrusion that contains no slip and no antiblock additives. Films produced with this resin exhibit a ve.. |
|||
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| A. Schulman PP 1817-01 Polypropylene Utility Grade Random Co-Polymer DescriptionPolypropylene PP 1817-01 is a utility grade random co-polymer which can be used for general purpose injection molding, extrusion, or blow molding applications. It does not have a gel spe.. |
|||
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| A. Schulman POLYBATCH™ ASC-331 Inorganic Antislip Masterbatch Based in Polyethylene DescriptionPOLYBATCH® ASC-331 is an inorganic antislip masterbatch based in polyethylene. ApplicationThis masterbatch was designed for use in moderate to heavy gauge applications to increase film .. |
|||
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| ELASTO UK Dryflex® 500700S SEBS Based Material, Unfilled Qualities, 70A Hardness, Translucent The 500-seriesis very favorable when transparency and good scratch resistance are required, as well as when there are high surface finish requirements. Unfilled grades have excellent flow and mecha.. |
|||
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| ELASTO UK Dryflex® 502800S SEBS Based Material, Unfilled Qualities, 80A Hardness, Black The 500-seriesis very favorable when transparency and good scratch resistance are required, as well as when there are high surface finish requirements. Unfilled grades have excellent flow and mecha.. |
|||
| Melt Flow | 2.0 g/10 min @Load 5.00 kg, Temperature 230 °C |
2.0 g/10 min @Load 11.0 lb, Temperature 446 °F |
ISO 1133 |
| ELASTO UK Dryflex® 9012-001 TPE, Modified Injection Molding Grade for Semi Rigid Molding The VTC TPE Group have developed endless formulations to fulfill different properties and application requirements to optimize the finished component. VTC Dryflex® 9012-001 is specifically designe.. |
|||
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| ExxonMobil LDPE LD 362BR Low Density Polyethylene Resin Product Description: LD 362 series are LEVA LDPE grades, offering good mechanical and sealing properties. Several additive combinations are available according to the required surface properties.Ava.. |
|||
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ASTM D1238 |
| Dow DOWLEX™ 2083G Linear Low Density Polyethylene Excellent tear strength, outstanding toughness Complies with U.S. FDA 21 CFR 177.1520 (c) 3.2a Information provided by Dow |
|||
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Dow AMPLIFY™ GR 209 Maleic anhydride grafted (MAH) polymer AMPLIFY™ GR 209 Functional Polymer is a post reactor maliec anhydride grafted (MAH) polymer. The base polymer is an ethylene-butene copolymer exhibiting high flexibility and elasticity. It can be.. |
|||
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM-D1238 |
| Braskem TN2020 EVA General Film Copolymer TN2020 is an Ethylene-Vinyl Acetate (EVA) copolymer developed to mostly meet the needs of the multi-layer packaging segment produced by coextrusion and/or lamination processes. Multilayer structures.. |
|||
| Melt Flow | 2.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
2.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Americas Styrenics EC6600 High Impact Polystyrene Product CharacteristicsExcellent printabilityMatte surface finishHigh heat distortion temperatureGood low temperature toughnessFood Contact CompliantTypical ApplicationsLithographic sheetPrinted toy.. |
|||
| Melt Flow | 2.0 - 3.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.0 - 3.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
|
| Breplast Bretene HDT Light High Density Polyethylene Recovered polyethylene compositeInformation provided by Breplast S.p.A. |
|||
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ASTM D1238 |
| Huntsman PE8010 Specialty Polyethylene
(discontinued **) Homopolymer and FDA compliant.Features: Yields film with excellent draw down and machinability.Applications: Film extrusion: gel free film applications.FDA Notes: Conforms to FDA regulation 21 CFR 1.. |
|||