Dow AMPLIFY™ GR 209 Maleic anhydride grafted (MAH) polymer

Category	Polymer , Thermoplastic
Manufacturer	Dow Chemical
Trade Name	AMPLIFY™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Dow AMPLIFY™ GR 209 Maleic anhydride grafted (MAH) polymer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

AMPLIFY™ GR 209 Functional Polymer is a post reactor maliec anhydride grafted (MAH) polymer. The base polymer is an ethylene-butene copolymer exhibiting high flexibility and elasticity. It can be utilized in monolayer and coextruded films and in blends with other polyolefins to enhance toughness of the structure. This product is a low gel MAH-grafted elastomer useful to improve impact resistance for polyamide or other engineering resins and to enhance interlayer adhesion in co-extruded films.Information provided by Dow

Physical Properties	Metric	English	Comments
Density	0.8985 g/cc	0.03246 lb/in³	ASTM D792
Filler Content	0.50 - 1.0 %	0.50 - 1.0 %	MAH graft; Dow Method
Melt Flow	2.0 g/10 min @Load 2.16 kg, Temperature 190 °C	2.0 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	87	87	5 sec; ASTM D2240
	90	90	1 sec; ASTM D2240
Tensile Strength, Ultimate	13.8 MPa	2000 psi	ASTM D638
Elongation at Break	800 %	800 %	ASTM D638
Flexural Modulus	0.0896 GPa	13.0 ksi	2% Secant; ASTM D790

Thermal Properties	Metric	English	Comments
Melting Point	115 °C	239 °F	Dow Method
Glass Transition Temp, Tg	-49.0 °C	-56.2 °F	Dow Method