- Dow DOWLEX™ 2083G Linear Low Density Polyethylene
Dow DOWLEX™ 2083G Linear Low Density Polyethylene
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE |
| Manufacturer | Dow Chemical |
| Trade Name | DOWLEX™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Dow DOWLEX™ 2083G Linear Low Density Polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Excellent tear strength, outstanding toughness Complies with U.S. FDA 21 CFR 177.1520 (c) 3.2a Information provided by Dow
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.925 g/cc | 0.0334 lb/in³ | ASTM D792 |
| Thickness | 20.3 microns | 0.800 mil | |
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 11.70 MPa | 1697 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 10.42 MPa | 1511 psi | ASTM D882 |
| Film Elongation at Break, MD | 418 % | 418 % | ASTM D882 |
| Film Elongation at Break, TD | 798 % | 798 % | ASTM D882 |
| Impact | 262 | 262 | [ft-lbf/in<sup>3</sup>]; Puncture Resistance; Dow Method |
| 1070 | 1070 | [ft-lbf/in<sup>3</sup>]; Toughness MD; ASTM D882 | |
| 1714 | 1714 | [ft-lbf/in<sup>3</sup>]; Toughness TD; ASTM D882 | |
| Elmendorf Tear Strength MD | 158 g | 158 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 576 g | 576 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 7.776 g/micron | 197.5 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 28.3 g/micron | 720 g/mil | ASTM D1922 |
| Dart Drop Test | 94.0 g | 0.207 lb | Method A; ASTM D1709 |
| Film Tensile Strength at Break, MD | 50.21 MPa | 7282 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 40.48 MPa | 5871 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 124 °C | 255 °F | Dow Method (DSC) |
| Vicat Softening Point | 108 °C | 226 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 1.2 % | 1.2 % | ASTM D1003 |
| Gloss | 93.4 % | 93.4 % | 45°; ASTM D2457 |
Users viewing this material also viewed the following:
- Plaskolite West Optix® CA - 75 UVA General Purpose Acrylic Resin
- SABIC Innovative Plastics Cycoloy® CY5210 PC+ABS (Europe-Africa-Middle East)
- Chevron Phillips EA3350 Crystal Polystyrene (discontinued **)
- LG Chemical Lupoy 3010-10 Polycarbonate Resin
- A. Schulman POLYBATCH™ Red LL50304/3 Concentrate Based In LLDPE
- DuPont Teijin Films Mylar® MLB Polyester Film, 48 Gauge
- Arlon 56146R028 0.028" (0.711 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- BASF HDO® 1,6-Hexanediol Molten
- Karina E 841-08/184-A-ERYB Beige PVC Compound
Copyright © lookpolymers.com All Rights Reserved