Huntsman PE8010 Specialty Polyethylene  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Huntsman PE8010 Specialty Polyethylene  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Homopolymer and FDA compliant.Features: Yields film with excellent draw down and machinability.Applications: Film extrusion: gel free film applications.FDA Notes: Conforms to FDA regulation 21 CFR 177.1520 (c)2.2 under condition of use B through H described in Table 2 of 21 CFR 176.170Film properties based on 1.0 guage (25 µm) thickness; blow-up ratio 2:1.Information provided by Huntsman Corporation
Physical Properties Metric English Comments
Density 0.922 g/cc
0.0333 lb/in³
ASTM D1505
Melt Flow 2.0 g/10 min
2.0 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 44
44
ASTM D2240
Tensile Strength, Ultimate 15.0 MPa
2180 psi
ASTM D638
Tensile Strength, Yield 10.0 MPa
1450 psi
ASTM D638
Film Elongation at Break, MD 168 %
168 %
ASTM D882
Film Elongation at Break, TD 249 %
249 %
ASTM D882
Elongation at Break 1000 %
1000 %
ASTM D638
Modulus of Elasticity 0.276 GPa
40.0 ksi
Secant; ASTM D638
Secant Modulus, MD 0.186 GPa
27.0 ksi
ASTM D882
Secant Modulus, TD 0.235 GPa
34.1 ksi
ASTM D882
Dart Drop Test 93.0 g
0.205 lb
ASTM D1709
Film Tensile Strength at Break, MD 18.0 MPa
2610 psi
ASTM D882
Film Tensile Strength at Break, TD 11.0 MPa
1600 psi
ASTM D882
Thermal Properties Metric English Comments
Vicat Softening Point 93.0 °C
199 °F
ASTM D1525
Optical Properties Metric English Comments
Haze 20 %
20 %
ASTM D1003
Gloss 35 %
35 %
at 45°; ASTM D523