Westlake Mxsten CV77518 Polyethylene Plastomer
| Category | Polymer , Thermoplastic , Polyethylene (PE) |
| Manufacturer | Westlake Chemical Corporation |
| Trade Name | Mxsten |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Westlake Mxsten CV77518 Polyethylene Plastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Mxsten CV Plastomer CV77518 resin is a polyethylene plastomer designed for blown and cast film extrusion that contains no slip and no antiblock additives. Films produced with this resin exhibit a very low seal initiation temperature with a broad hot tack window. Other features of this resin include higher stiffness and high melting point.Application/UsesBlown filmCast filmPackagingFDA: This material complies with FDA regulations in 21 CFR, section 177.1520. Kosher Compliant.All information provided by Westlake Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.910 g/cc | 0.0329 lb/in³ | ASTM D1505 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 700 % | 700 % | ASTM D882 |
| Film Elongation at Break, TD | 1200 % | 1200 % | ASTM D882 |
| Elmendorf Tear Strength MD | 300 g | 300 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 550 g | 550 g | ASTM D1922 |
| Dart Drop | 15.7 g/micron | 400 g/mil | ASTM D1709A |
| Film Tensile Strength at Break, MD | 35.2 MPa | 5100 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 40.0 MPa | 5800 psi | ASTM D882 |
| 1% Secant Modulus, MD | 152 MPa | 22000 psi | ASTM D882 |
| 1% Secant Modulus, TD | 172 MPa | 25000 psi | ASTM D882 |
| Heat Seal Strength Initiation Temperature | 88.0 °C | 190 °F | Westlake |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 13 % | 13 % | ASTM D1003 |
| Gloss | 55 % | 55 % | at 45º; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 216 - 232 °C | 420 - 450 °F | |
| Blow-up Ratio (BUR) | 2.4 | 2.4 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Process | Blown Film | |
| Film | ||
| Region | US & Canada | Bamberger Polymers Distribution |
Users viewing this material also viewed the following:
- Mallard Creek Polymers ROVENE® 8305 SBR Emulsion
- Lord Adhesives 7545B Two-Component, Equal-Mix, Non-Sag Urethane Adhesive
- Loxim 340 01HB Nylon 6
- Lubriplate TEMP LOW Anhydrous Calcium Multi-Purpose Grease For Special Conditions
- Teknor Apex APEX® 3611-65 Polyvinyl Chloride, Flexible
- Styron CALIBREâ„¢ 7103-15 Polycarbonate
- Covestro Baydur® 660 IBS Polyurethane Structural Foam RIM, Density 30 pcf, MDI-based 2-Component Liquid System
- CP-Polymer-Technik Wellamid® 6000 SCP Nylon 6, Finely Crystalline, Dry
- Arkema Group Orevac® 9318 Film EVA-MAH Terpolymer
- Samyang Triloy® 210N PC/ABS alloy, Flame Retardant
Copyright © lookpolymers.com All Rights Reserved