Zircar Ceramics ASQ Castertip

Category	Ceramic , Oxide , Aluminum Oxide , Silicon Oxide
Manufacturer	Zircar Ceramics
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Zircar Ceramics ASQ Castertip.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

14 pcf density refractory ceramic fiber "soft tip". Alumina bonding of shot free fiber results in extreme performance in manufacture of the finest grades of medical, food and packaging foils. Information provided by Zircar Ceramics.

Physical Properties	Metric	English	Comments
Bulk Density	0.190 - 0.260 g/cc	0.00686 - 0.00939 lb/in³
Loss On Ignition	3.00 % @Temperature 760 °C, Time 86400 sec	3.00 % @Temperature 1400 °F, Time 24.0 hour

Mechanical Properties	Metric	English	Comments
Flexural Strength	0.370 MPa	53.7 psi	after 24 hrs at 1200°C, as Received, Parallel to Thickness
	0.460 MPa	66.7 psi	As received, Parallel to Thickness
	0.480 MPa	69.6 psi	after 24 hrs at 1000°C, as Received, Parallel to Thickness
	0.500 MPa	72.5 psi	after 24 hrs at 760°C, as Received, Parallel to Thickness
Compressive Strength	0.110 MPa	16.0 psi	as Received, Parallel to Thickness
	0.120 MPa	17.4 psi	after 24 hrs at 760°C, as Received, Parallel to Thickness

Thermal Properties	Metric	English	Comments
Thermal Conductivity	0.110 W/m-K @Temperature 600 °C	0.763 BTU-in/hr-ft²-°F @Temperature 1110 °F	parallel to thickness
	0.160 W/m-K @Temperature 800 °C	1.11 BTU-in/hr-ft²-°F @Temperature 1470 °F	Parallel to Thickness
	0.270 W/m-K @Temperature 1100 °C	1.87 BTU-in/hr-ft²-°F @Temperature 2010 °F	parallel to thickness
Maximum Service Temperature, Air	1260 °C	2300 °F
Shrinkage	2.00 % @Temperature 760 - 1000 °C, Time 86400 sec	2.00 % @Temperature 1400 - 1830 °F, Time 24.0 hour	Perpendicular to Thickness
	3.0 % @Temperature 1100 °C, Time 86400 sec	3.0 % @Temperature 2010 °F, Time 24.0 hour	Perpendicular to Thickness
	5.00 % @Temperature 1200 °C, Time 86400 sec	5.00 % @Temperature 2190 °F, Time 24.0 hour	Perpendicular to Thickness

Component Elements Properties	Metric	English	Comments
Al2O3	58 %	58 %
SiO2	42 %	42 %

Descriptive Properties	Value	Comments
Binder	Alumina
Color	White