Westlake Elevate™ EF563 6.5% Ethylene Vinyl Acetate Copolymer

Category	Polymer , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Film Grade
Manufacturer	Westlake Chemical Corporation
Trade Name	Elevate™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Westlake Elevate™ EF563 6.5% Ethylene Vinyl Acetate Copolymer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Westlake EF 563 resin is a fractional melt index 6.5% EVA copolymer with excellent drawdown, low melting/dispersion, and clarity optics in a soft but very tough film. Kosher compliant.Application/UsesFilm packagingBatch inclusion bagsFDA: This material complies with FDA regulations in 21 CFR, section 177.1350.All information provided by Westlake Chemical

Physical Properties	Metric	English	Comments
Density	0.932 g/cc	0.0337 lb/in³	with antiblock; ASTM D1505
Vinyl Acetate Content	6.5 %	6.5 %
Thickness	38.1 microns	1.50 mil	as tested
Melt Flow	1.1 g/10 min	1.1 g/10 min	ASTM D1238

Mechanical Properties	Metric	English	Comments
Dart Drop	7.09 g/micron	180 g/mil	ASTM D1709
Film Tensile Strength at Break, MD	31.0 MPa	4500 psi	ASTM D882
Film Tensile Strength at Break, TD	22.8 MPa	3300 psi	ASTM D882
1% Secant Modulus, MD	96.5 MPa	14000 psi	ASTM D882
1% Secant Modulus, TD	103 MPa	15000 psi	ASTM D882

Thermal Properties	Metric	English	Comments
Melting Point	103 °C	217 °F	Peak DSC; Westlake Method

Optical Properties	Metric	English	Comments
Haze	10 %	10 %	with 9000 ppm antiblock; ASTM D1003
Gloss	60 %	60 %	at 45º (with 9000 ppm antiblock); ASTM D2457

Processing Properties	Metric	English	Comments
Melt Temperature	193 - 204 °C	380 - 400 °F
Blow-up Ratio (BUR)	2.5	2.5	as tested

Descriptive Properties	Value	Comments
Process	Film
Region	US & Canada	Bamberger Polymers Distribution