TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 10.0 PHR TP-95 Plasticizer

Category Polymer , Thermoset , Polyester, TS , Polyurethane, TS , Thermoset Polyurethane, Elastomer, Unreinforced , Rubber or Thermoset Elastomer (TSE)
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 10.0 PHR TP-95 Plasticizer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Millathane® 76 is a very suitable choice for use in products such as bushings, small copier rolls; automotive applications — bumpers, o-rings, hydraulic seals, belts, gaskets, solid tires — and many other high performance polyurethane applications. Millathane 76 can be vulcanized by sulfur or peroxide cured systems.Plasticizers should be used in all Millathane®76 compounds to better incorporate fillers and improve processing. Some plasticizers are not compatible with Millathane76, e.g. naphthenic and all paraffinic oils, however, a number of ester plasticizers perform very well.FormulationMillathane 76 100.0Zinc Stearate0.5N-550 Black40.0MBTS4.0MBT2.0Thanecure® ZM1.0Sulfur1.5Plasticizer10.0All information provided by TSE Industries
Mechanical Properties Metric English Comments
Hardness, Shore A 63
63
70
70
heat aged 70 hours @ 100ºC
Tensile Strength, Yield 23.39 MPa
3393 psi
Elongation at Yield 542 %
542 %
100% Modulus 0.00274 GPa
0.398 ksi
200% Modulus 0.00654 GPa
0.948 ksi
300% Modulus 0.01127 GPa
1.634 ksi
Tear Strength 59.7 kN/m
341 pli
Die C
Compression Set 44.2 %

@Temperature 70.0 °C,
Time 79200 sec
44.2 %

@Temperature 158 °F,
Time 22.0 hour
Thermal Properties Metric English Comments
Brittleness Temperature -35.0 °C
-31.0 °F
Processing Properties Metric English Comments
Cure Time 10.0 min

@Temperature 155 °C
0.167 hour

@Temperature 311 °F
Descriptive Properties Value Comments
Weight Loss (%) 1.9
heat aged 70 hours @ 100ºC