Samsung Cheil Industries Starex® HR-1360 HIPS, Unreinforced Heat Resistant
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® HR-1360 HIPS, Unreinforced Heat Resistant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0070 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 3.9 g/10 min @Load 5.00 kg, Temperature 200 °C |
3.9 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 100 | 100 | ASTM D785 |
| Tensile Strength, Yield | 30.4 MPa | 4410 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 70 % | 70 % | 20 mm/min; ASTM D638 |
| Izod Impact, Notched | 1.13 J/cm @Thickness 3.17 mm |
2.11 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 91.0 °C | 196 °F | B/50; ISO R306 |
| Flammability, UL94 | HB @Thickness 1.00 - 3.00 mm |
HB @Thickness 0.0394 - 0.118 in |