- Samsung Cheil Industries Starex® BC-0130 X ABS, Unreinforced General Purpose
Samsung Cheil Industries Starex® BC-0130 X ABS, Unreinforced General Purpose
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® BC-0130 X ABS, Unreinforced General Purpose.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Stiff ABS material that is used for battery casesInformation provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0060 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 2.6 g/10 min @Load 5.00 kg, Temperature 200 °C |
2.6 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 113 | 113 | ASTM D785 |
| Tensile Strength at Break | 37.3 MPa | 5410 psi | 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 48.1 MPa | 6970 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 14 % | 14 % | 5 mm/min; ASTM D638 |
| Tensile Modulus | 2.35 GPa | 341 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 70.6 MPa | 10200 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 2.16 GPa | 313 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.981 J/cm @Thickness 6.35 mm |
1.84 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 1.18 J/cm @Thickness 3.17 mm |
2.20 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 96.0 °C @Thickness 6.40 mm |
205 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C @Thickness 6.40 mm |
187 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 99.0 °C | 210 °F | B/50; ISO R306 |
| 102 °C | 216 °F | B/120; ISO R306 | |
| Flammability, UL94 | HB @Thickness 1.50 - 3.00 mm |
HB @Thickness 0.0591 - 0.118 in |
Users viewing this material also viewed the following:
- Haynes Hastelloy® C-22HS™ Nickel Alloy Gas Tungsten Arc Welded (GTAW) Sheet
- SABIC Innovative Plastics LNP STAT-KON DX10315C PC (Asia Pacific)
- A. Schulman POLYFORT™ FPP 1606 Glass Filled Chemically Coupled Impact Copolymer Polypropylene
- Elisto THERMOSTAR® LC 610 Insulation Material
- 3M Controltac™ 8620Cv2 ES Changeable Graphic Film with Comply™ v2 Adhesive
- Beijing Ranger Chem PBT-201-G25 211 Flame Retarding FR PBT
- ExxonMobil Escorene® LD-332 EVA Packaging Film Resin, High Clarity (discontinued **)
- Indium Corp. Indalloy 218 Silver Solder Alloy
- LNP Thermocomp® UF-1006 A HS Polyphthalamide, Glass Fiber Reinforcement (discontinued **)
Copyright © lookpolymers.com All Rights Reserved