SABIC Innovative Plastics Ultem 1000V PEI
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Ultem 1000V PEI.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Transparent, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing; color dependant, see UL Yellow Card. US FDA and EU Food Contact compliant, NSF 51 listing, compliant in natural color. Effective June, 2007 this grade will no longer be supported with biocompatibility information and should not be used for medical applications which require biocompatibility. Alternative grade HU1000.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.27 g/cc | 1.27 g/cc | ASTM D 792 |
| Density | 1.27 g/cc | 0.0459 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.70 % | 0.70 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 1.25 % @Temperature 23.0 °C |
1.25 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 9.0 g/10 min @Load 6.60 kg, Temperature 337 °C |
9.0 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D 1238 |
| 13 g/10 min @Load 5.00 kg, Temperature 220 °C |
13 g/10 min @Load 11.0 lb, Temperature 428 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 85.0 MPa | 12300 psi | 5 mm/min; ISO 527 |
| 90.0 MPa | 13100 psi | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Strength, Yield | 105 MPa | 15200 psi | 5 mm/min; ISO 527 |
| 110 MPa | 16000 psi | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Break | 60 % | 60 % | Type I, 5 mm/min; ASTM D 638 |
| 60 % | 60 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 7.0 % | 7.0 % | Type I, 5 mm/min; ASTM D 638 |
| Tensile Modulus | 3.20 GPa | 464 ksi | 1 mm/min; ISO 527 |
| 3.58 GPa | 519 ksi | 5 mm/min; ASTM D 638 | |
| Flexural Yield Strength | 160 MPa | 23200 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 160 MPa | 23200 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 3.30 GPa | 479 ksi | 2 mm/min; ISO 178 |
| 3.43 GPa | 497 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 0.530 J/cm @Temperature 23.0 °C |
0.993 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| 0.530 J/cm @Temperature -30.0 °C |
0.993 ft-lb/in @Temperature -22.0 °F |
ASTM D 256 | |
| Izod Impact, Unnotched | 13.35 J/cm @Temperature 23.0 °C |
25.01 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| 6.00 kJ/m² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 0.400 J/cm² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 50.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
27.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 55.8 µm/m-°C @Temperature -20.0 - 150 °C |
31.0 µin/in-°F @Temperature -4.00 - 302 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 50.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
27.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 54.0 µm/m-°C @Temperature -20.0 - 150 °C |
30.0 µin/in-°F @Temperature -4.00 - 302 °F |
ASTM E 831 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 201 °C @Thickness 6.40 mm |
394 °F @Thickness 0.252 in |
unannealed; ASTM D 648 | |
| Vicat Softening Point | 211 °C | 412 °F | Rate B/120; ISO 306 |
| 215 °C | 419 °F | Rate B/50; ISO 306 | |
| 218 °C | 424 °F | Rate B/50; ASTM D 1525 | |
| Glass Transition Temp, Tg | 217 °C | 423 °F | |
| Flammability, UL94 | V-2 @Thickness 0.400 mm |
V-2 @Thickness 0.0157 in |
UL 94 |
| V-1 @Thickness 0.750 mm |
V-1 @Thickness 0.0295 in |
UL 94 | |
| V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
UL 94 | |
| 5VA @Thickness 3.00 mm |
5VA @Thickness 0.118 in |
UL 94 | |
| Oxygen Index | 47 % | 47 % | LOI; ASTM D 2863 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90 % | 90 % | transparent; thickness not quantified |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Arc Resistance | 120 - 180 sec | 120 - 180 sec | Tungsten, PLC code 5; ASTM D 495 |
| Comparative Tracking Index | 100 - 175 V | 100 - 175 V | PLC code 4; UL 746A |
| Hot Wire Ignition, HWI | 60 - 120 sec | 60 - 120 sec | PLC code 1; UL 746A |
| High Amp Arc Ignition, HAI | 15 - 30 arcs | 15 - 30 arcs | surface, PLC code 3; UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 25.4 - 80.0 mm/min | 1.00 - 3.15 in/min | PLC code 2; UL 746A |
Users viewing this material also viewed the following:
- Mitsubishi Hostaphan® RN, 190 micron Nominal Thickness Universal Polyethylene Terephthalate Film
- Stir SpA SA 68 R (PVC)
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 0.50 PHR Zinc Stearate
- ChevronTexaco Aero 20W-50 Engine Oil AD
- DSM Arnite® TV4 441 (PBT+PET)-GF20
- Dow FLEXOMER™ DFDA-1098 NT Very Low Density Polyethylene (VLDPE) Resin
- Braskem F 7018 LDPE Extrusion Coating Polyethylene
- 3M Dyneon™ THV 500GZ Fluorothermoplastic Granules
- Overview of materials for Epoxy, Molded, Glass Fiber Filler
- Eastman 9921W PET Injection Molded (discontinued **)
Copyright © lookpolymers.com All Rights Reserved