Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 110 MPa | 16000 psi | Type I, 5.1 mm/min; ASTM D638 |
PolyOne Nymax™ GF 600 A 14 Natural Polyamide 6 (Nylon 6) The Nymax® GF 600 Series of glass fiber-reinforced nylon 6 compounds have been specifically engineered for applications requiring high stiffness, tensile strength, and toughness, while providing en.. |
|||
Tensile Strength, Yield | 110 MPa | 16000 psi | ASTM D638 |
Oxford Polymers Oxnilon 66-13GF 13% Glass Fiber Filled Nylon 66 for Injection Molding 13% Glass Fiber Filled Nylon 66 for Injection MoldingInformation provided by Oxford Polymers. |
|||
Tensile Strength, Yield | 110 MPa | 16000 psi | ASTM D638 |
Polymer Resources NY66-G13-[color]-H Nylon 66, 13% Glass Reinforced, Heat Stabilized Nylon 66, 13% Glass Reinforced, Heat Stabilized, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylo.. |
|||
Tensile Strength, Yield | 110 MPa | 16000 psi | ISO-DIS 527 |
Schwartz Technical Plastics LAMIGAMID® 327 Cast Polyamide 6, MoS2, Heat Stabilized, Dry Application: heavy-duty wheels, running speed up to 3m/sInformation provided by Schwartz Technical Plastics GmbH |
|||
Tensile Strength, Yield | 110 MPa | 16000 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM 1010K PEI (Asia Pacific) Transparent, high flow Polyetherimide (Tg 217C). ECO Conforming. |
|||
Tensile Strength, Yield | 110 MPa | 16000 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics Ultem 1010RV PEI (Asia Pacific) Enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing; color dependant, see UL Yellow Card.This data was supplied by SABIC-IP for the Asia Pacif.. |
|||
Tensile Strength, Yield | 110 MPa | 16000 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics Ultem 1100EF PEI Enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, U.S. FDA and EU Food Contact compliant.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength, Yield | 110 MPa | 16000 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM 1100F PEI (Asia Pacific) Standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0, V2 and 5VA listing. US FDA and EU Food Contact compliant. Effective June 2007, this grade will no longer be supported with biocompati.. |
|||
Tensile Strength, Yield | 110 MPa | 16000 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics ULTEM 1100F PEI (Europe-Africa-Middle East) Standard flow Polyetherimide (Tg 217C). Resin is RoHS compliant. UL94 V0, V2 and 5VA listing. US FDA and EU Food Contact compliant. Effective June, 2007 this grade will no longer be supported with b.. |
|||
Tensile Strength, Yield | 110 MPa | 16000 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics Ultem 1100FV PEI (Europe-Africa-Middle East) Standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing; color dependant, see UL Yellow Card. US FDA and EU Food Contact compliant.This data was supplied by SABIC-IP for th.. |
|||
Tensile Strength, Yield | 110 MPa | 16000 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM HU1010 PEI Transparent, enhanced flow Polyetherimide (Tg 217C). ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI),.. |
|||
Tensile Strength, Yield | 110 MPa | 16000 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Ultem MD130A PEI (Europe-Africa-Middle East) Transparent, standard flow Polyetherimide (Tg 217C). ECO Conforming. US FDA and EU Food Contact compliant, ISO 10993 compliant in recognized colors.This data was supplied by SABIC-IP for the Europe-.. |
|||
Tensile Strength, Yield | 110 MPa | 16000 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® ENH4560 PBT (Europe-Africa-Middle East) Valox* ENH4560 resin is a non-brominated/non-chlorinated flame retardant product based on Valox* PBT resin. |
|||
Tensile Strength, Yield | 110 MPa | 16000 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP EX06430H PEI LNP* THERMOCOMP* EX06430H is a compound based on Polyetherimide resin containing Proprietary Filler(s). Added feature of this grade is: Healthcare. |
|||
Tensile Strength, Yield | 110 MPa | 16000 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics ULTEM 1110 PEI (Europe-Africa-Middle East) Enhanced flow Polyetherimide (Tg 217C). Resin is RoHS compliant. |
|||
Tensile Strength, Yield | 110 MPa | 16000 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Valox® 451E PBT (Europe-Africa-Middle East) VALOX 451E is 20% glass reinforced, flame retardant PBT injection moulding resin. |
|||
Tensile Strength, Yield | 110 MPa | 16000 psi | ISO 527-2 |
Tisan TISESTER® 15% Glass Fiber Reinforced Polybutylene Terephthalate TISESTER has a wide area of application in automotive, electric/electronics and durable goods industries. General Specifications include: Excellent surface appearanceHigh corrosion and abrasion resi.. |
|||
Tensile Strength, Yield | 110 MPa | 16000 psi | ISO 527 |
Polyram RamTal PM3007G5 Polyacetal for Injection Molding, 25% Glass Fiber Reinforced 25% Glass fiber reinforced polyacetal for injection molding applications.Information provided by Polyram. |
|||
Tensile Strength, Yield | 110 MPa | 16000 psi | ASTM-D638 |
Polyram RamTough RZ300G6 Polycarbonate, 30% Glass Fiber 30% glass fiber reinforced polycarbonate for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Tensile Strength, Yield | 110 MPa | 16000 psi | GB/1040 |
Zhejiang Juner PA66-301-G20 Flame-Retardant & Glass Reinforced, Environmental PA66 Applications: Framework of CoilsInformation provided by Zhejiang Juner New Materials Co, Ltd. |
|||
Tensile Strength, Yield | 110 MPa | 16000 psi | GB-1040 |
Zhejiang Juner PA-A6 GF20% Applications: Shell of Middle & Top Grade MCB, Pedestal & Shell of Low Voltage Electrical ApplianceInformation provided by Zhejiang Juner New Materials Co, Ltd. |
|||
Tensile Strength, Yield | 110 MPa | 16000 psi | ASTM-D638 |
Polyram PlusTek RA303G4 Nylon 6.6, 20% Glass Fiber 20% glass fiber reinforced, heat stabilized polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Tensile Strength, Yield | 110 MPa | 16000 psi | ASTM D638 |
Ashley Polymers Ashlene® E126WO PET Polyester, 30% Glass Reinforced PET Polyester with 30% glass reinforcement, flame retardant, natural. Note: Colors will modify properties.Data provided by the manufacturer |
|||
Tensile Strength, Yield | 110 MPa | 16000 psi | v = 50 mm/min; ISO 527-2 |
CENTROPLAST CENTROPEEK Polyetheretherketone This plastic has high temperature resistance, good chemical resistance, and good mechanical characteristics. Its has good sliding friction properties and is suitable for use with foodstuffs or medi.. |
|||
Tensile Strength, Yield | 110 MPa | 16000 psi | ASTM D638 |
Beijing Ranger Chem PBT 403 M-G15 Heat Resistant and Environmental Protection Flame Retarding FR PBT Modified PBT Characteristics: Unreinforced grades have abundant strength and flexibility, and have strong characteristics against brittleness. UL-certified slow-burning (94HB) and self-extinguishin.. |
|||
Tensile Strength, Yield | 110 MPa | 16000 psi | Wet; ASTM D638 |
Asahi Kasei Leona® 13G25 25% Glass Filled Nylon 66 Enhanced strength, stiffness and durability; with 25% GF.Applications:Automotive parts Information provided by Asahi Kasei |
|||
Tensile Strength, Yield | 110 MPa | 16000 psi | ASTM D638 |
Beijing Ranger Chem PBT-201-G25 Flame Retarding FR PBT Modified PBT Characteristics: Unreinforced grades have abundant strength and flexibility, and have strong characteristics against brittleness. UL-certified slow-burning (94HB) and self-extinguishin.. |
|||
Tensile Strength, Yield | 110 MPa | 16000 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM 1000E PEI Transparent, standard flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming. US FDA and EU Food Contact compliant, NSF 51 Listing. Effective June, 2007 this grade will no longer.. |
|||
Tensile Strength, Yield | 110 MPa | 16000 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM 1000EF PEI (Europe-Africa-Middle East) Transparent, enhanced flow Polyetherimide (Tg 217C) with internal mold release. Resin is RoHS. US FDA and EU Food Contact compliant. |
|||
Tensile Strength, Yield | 110 MPa | 16000 psi | |
PSM Industries Pacific Sintered Metals Yellow Brass BZ-111-UC Powdered Metal 80-20 leaded brass, Coined for close dimensional control, strength and density Equivalent MPIF Specification: CZP-2000-12Information Provided by Pacific Sintered Metals, a division of PSM Industrie.. |