SABIC Innovative Plastics Noryl GTX GTX8721 PPE+PA
| Category | Polymer , Thermoplastic , Polyester, TP , Polyphenylene Ether/PPO |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | NORYL GTX |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Noryl GTX GTX8721 PPE+PA.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Noryl GTX GTX8721 resin is a glass and talc filled, high performance blend of PPE/PA that exhibits an excellent balance of high-heat resistance, strength, flow, conductivity, and low warpage. This grade can be electrostatically painted or powder coated without the need for conductive primer.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.37 g/cc | 1.37 g/cc | ASTM D 792 |
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 1.2 % | 1.2 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 4.0 % @Temperature 23.0 °C |
4.0 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0023 - 0.0028 cm/cm @Thickness 3.20 mm |
0.0023 - 0.0028 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0064 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0064 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 5.0 g/10 min @Load 5.00 kg, Temperature 280 °C |
5.0 g/10 min @Load 11.0 lb, Temperature 536 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| 6.8 g/10 min @Load 5.00 kg, Temperature 280 °C |
6.8 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 145 MPa | 21000 psi | Type I, 5 mm/min; ASTM D 638 |
| 145 MPa | 21000 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 145 MPa | 21000 psi | Type I, 5 mm/min; ASTM D 638 |
| 145 MPa | 21000 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 5.0 % | 5.0 % | Type I, 5 mm/min; ASTM D 638 |
| 5.0 % | 5.0 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D 638 |
| 2.0 % | 2.0 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 10.5 GPa | 1520 ksi | 5 mm/min; ASTM D 638 |
| 10.5 GPa | 1520 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 220 MPa | 31900 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 220 MPa | 31900 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 9.50 GPa | 1380 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 9.50 GPa | 1380 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.650 J/cm @Temperature -30.0 °C |
1.22 ft-lb/in @Temperature -22.0 °F |
ASTM D 256 |
| 0.850 J/cm @Temperature 23.0 °C |
1.59 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 | |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A |
| 7.00 kJ/m² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 0.600 J/cm² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Impact Test | 6.00 J @Temperature 23.0 °C |
4.43 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 22.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
12.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 22.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
12.2 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 68.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.8 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 68.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 220 °C @Thickness 3.20 mm |
428 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Vicat Softening Point | 215 °C | 419 °F | Rate B/50; ISO 306 |
| 215 °C | 419 °F | Rate B/120; ISO 306 | |
| 220 °C | 428 °F | Rate B/50; ASTM D 1525 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 500 - 10000 ohm-cm | 500 - 10000 ohm-cm | SABIC Method |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP Lubricomp ICP36 PA 6/12 (Asia Pacific)
- SABIC Innovative Plastics LNP Stat-kon DEP32XXC PC (Asia Pacific)
- Styrolution Luran® S 778 UV Colored ASA
- Styron DL 219NA Carboxylated SB
- Chosun Refractories N1-1 Fireclay brick
- Arkema Group Pebax® 7233 SN 01 Polyether Block Amide (PEBA) (Conditioned)
- Solvay Specialty Polymers Algoflon® 50 INOX PTFE; Stainless Steel Filled (discontinued **)
- Arkema Group Oroglas® V 825 HID Acrylic, UV, Heat Resistant (discontinued **)
Copyright © lookpolymers.com All Rights Reserved