SABIC Innovative Plastics Lexan® EXL1192C PC Copolymer

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® EXL1192C PC Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High flow, polycarbonate siloxane copolymer resin. Notched izod ductile to -20C ductility. Enhanced processability compared to standard PC resins. Available in a range of transparent colors. US FDA compliant only. Not yet approved for EU FC applicationsThis data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Specific Gravity 1.18 g/cc
1.18 g/cc
ASTM D 792
Density 1.18 g/cc
0.0426 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.10 %
0.10 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.29 %

@Temperature 23.0 °C
0.29 %

@Temperature 73.4 °F
ISO 62
Linear Mold Shrinkage, Flow 0.0040 - 0.0080 cm/cm

@Thickness 3.20 mm
0.0040 - 0.0080 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 19 g/10 min

@Load 1.20 kg,
Temperature 300 °C
19 g/10 min

@Load 2.65 lb,
Temperature 572 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
20 g/10 min

@Load 1.20 kg,
Temperature 300 °C
20 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Hardness, Rockwell L 92
92
ASTM D 785
Tensile Strength at Break 59.0 MPa
8560 psi
Type I, 50 mm/min; ASTM D 638
59.0 MPa
8560 psi
50 mm/min; ISO 527
Tensile Strength, Yield 59.0 MPa
8560 psi
Type I, 50 mm/min; ASTM D 638
59.0 MPa
8560 psi
50 mm/min; ISO 527
Elongation at Break 122.5 %
122.5 %
50 mm/min; ISO 527
125.1 %
125.1 %
Type I, 50 mm/min; ASTM D 638
Elongation at Yield 5.3 %
5.3 %
50 mm/min; ISO 527
5.4 %
5.4 %
Type I, 50 mm/min; ASTM D 638
Tensile Modulus 2.35 GPa
341 ksi
5 mm/min; ASTM D 638
2.46 GPa
357 ksi
1 mm/min; ISO 527
Flexural Yield Strength 91.0 MPa
13200 psi
2 mm/min; ISO 178
96.0 MPa
13900 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 2.22 GPa
322 ksi
2 mm/min; ISO 178
2.30 GPa
334 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 4.26 J/cm

@Temperature -30.0 °C
7.98 ft-lb/in

@Temperature -22.0 °F
ASTM D 256
5.77 J/cm

@Temperature -20.0 °C
10.8 ft-lb/in

@Temperature -4.00 °F
ASTM D 256
6.16 J/cm

@Temperature -10.0 °C
11.5 ft-lb/in

@Temperature 14.0 °F
ASTM D 256
7.37 J/cm

@Temperature 23.0 °C
13.8 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Notched (ISO) 16.0 kJ/m²

@Temperature -30.0 °C
7.61 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
46.0 kJ/m²

@Temperature 23.0 °C
21.9 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 1.90 J/cm²

@Temperature -30.0 °C
9.04 ft-lb/in²

@Temperature -22.0 °F
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
6.20 J/cm²

@Temperature 23.0 °C
29.5 ft-lb/in²

@Temperature 73.4 °F
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
Impact Test 70.0 J

@Temperature 23.0 °C
51.6 ft-lb

@Temperature 73.4 °F
Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 61.5 µm/m-°C

@Temperature -40.0 - 40.0 °C
34.2 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
61.5 µm/m-°C

@Temperature -40.0 - 40.0 °C
34.2 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 64.5 µm/m-°C

@Temperature -40.0 - 40.0 °C
35.8 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
64.5 µm/m-°C

@Temperature -40.0 - 40.0 °C
35.8 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 116 °C
241 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
119 °C

@Thickness 3.20 mm
246 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Vicat Softening Point 137 °C
279 °F
Rate A/50; ASTM D 1525
137 °C
279 °F
Rate B/50; ISO 306
139 °C
282 °F
Rate B/120; ISO 306
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
UL 94
V-2

@Thickness 2.50 mm
V-2

@Thickness 0.0984 in
UL 94
Optical Properties Metric English Comments
Haze 1.4 %

@Thickness 2.54 mm
1.4 %

@Thickness 0.100 in
ASTM D 1003
Transmission, Visible 86 %

@Thickness 2.54 mm
86 %

@Thickness 0.100 in
ASTM D 1003