- Polymer Property : Flexural Modulus = 2.22 GPa
Polymer Property : Flexural Modulus = 2.22 GPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Modulus | 2.22 GPa | 322 ksi | ASTM D790 |
| NYCOA 5100 HS Heat Stabilized, Impact Modified Nylon 66 Resin NYCOA 5100 HS is an impact modified, heat stabilized Nylon 66 resin used for injection molding. This material is specially formulated to provide improved flexibility and ductility vs standard Nylon .. |
|||
| Flexural Modulus | 2.22 GPa | 322 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics Lexan® FXD1414T PC Copolymer (Asia Pacific) PC-siloxane copolymer in special light diffusion colors. Medium flow. Improved toughness compared to medium flow standard PC in same color. Color package may affect performance. |
|||
| Flexural Modulus | 2.22 GPa | 322 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics Lexan® HFD1212 PC Copolymer (Europe-Africa-Middle East) 18 MFR LEXAN High Flow Ductile Copolymer |
|||
| Flexural Modulus | 2.22 GPa | 322 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics Lexan® HFD1232 PC Copolymer 18 MFR LEXAN High Flow Ductile Copolymer UV-stabilized, available in transparent colors only |
|||
| Flexural Modulus | 2.22 GPa | 322 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics Lexan® HFD1232 PC Copolymer (Asia Pacific) 18 MFR LEXAN High Flow Ductile Copolymer UV-stabilized, available in transparent colors only |
|||
| Flexural Modulus | 2.22 GPa | 322 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics Lexan® HFD1262 PC Copolymer (Asia Pacific) 19 MFR LEXAN High Flow Ductile Copolymerwith 400 nm cut off, available in transparent colors only |
|||
| Flexural Modulus | 2.22 GPa | 322 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics Lexan® HFD1711 PC Copolymer 25 MFR LEXAN High Flow Ductile Copolymer |
|||
| Flexural Modulus | 2.22 GPa | 322 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics Lexan® HPF1 PC Copolymer 25 MFR LEXAN High Flow Ductile Copolymer Healthcare Grade |
|||
| Flexural Modulus | 2.22 GPa | 322 ksi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics Lexan® ML7647 PC Non FR Impact modified PC, excellent Fatigue performance with balanced Flow and impact. Available in Opaque onlyThis data was supplied by SABIC-IP for the Americas region. |
|||
| Flexural Modulus | 2.22 GPa | 322 ksi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics Lexan® ML7647 PC (Asia Pacific) Non FR Impact modified PC, excellent Fatigue performance with balanced Flow and impact. Available in Opaque only |
|||
| Flexural Modulus | 2.22 GPa | 322 ksi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics Lexan® ML7647 PC (Europe-Africa-Middle East) Non FR Impact modified PC, excellent Fatigue performance with balanced Flow and impact. Available in Opaque onlyThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
| Flexural Modulus | 2.22 GPa | 322 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| SABIC Innovative Plastics Lexan® FXD1414T PC Copolymer (Europe-Africa-Middle East) PC-siloxane copolymer in special light diffusion colors. Medium flow. Improved toughness compared to medium flow standard PC in same color. Color package may affect performance.This data was suppli.. |
|||
| Flexural Modulus | 2.22 GPa | 322 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics Lexan® HFD1212 PC Copolymer (Asia Pacific) 18 MFR LEXAN High Flow Ductile Copolymer |
|||
| Flexural Modulus | 2.22 GPa | 322 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics Lexan® HFD1262 PC Copolymer 19 MFR LEXAN High Flow Ductile Copolymerwith 400 nm cut off, available in transparent colors only |
|||
| Flexural Modulus | 2.22 GPa @Thickness 6.40 mm |
321 ksi @Thickness 0.252 in |
15 mm/min; ASTM D790 |
| LG Chemical TR557 MABS, High Transparency, High Impact Feature: Injection Molding, High Transparency, High ImpactApplication: Electric/Electronic Applications, Copier, Printer etc.CAS No. 9011-14–7 and 9003-56-9Information provided by LG Chemical |
|||
| Flexural Modulus | 2.22 GPa | 322 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics LNP LUBRICOMP NXCY620 PC+ABS LNP* LUBRICOMP* NXCY620 is a compound based on Cycoloy* XCY620 containing Silicone. Added feature of this material is: Lubricant. |
|||
| Flexural Modulus | 2.22 GPa | 322 ksi | 2 mm/min, 64mm span; ISO 178 |
| SABIC Innovative Plastics SABIC PPCOMPOUND 7985 PP SABIC® PPcompound 7985 is a mineral filled, impact modified polypropylene TPO. This material combines scratch resistance and heat stability with interior automotive UV stability. The IMDS is 2097.. |
|||
| Flexural Modulus | 2.22 GPa | 322 ksi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP LUBRICOMP RP004S PA 66 LNP* LUBRICOMP* RP004S is a compound based on Nylon 66 containing PTFE/Silicone. Added features of this grade include: Heat Stabilized, Wear Resistant. |
|||
| Flexural Modulus | 2.22 GPa | 322 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics XYLEX X8409AC PC+POLYESTER PC + Polyester, Injection (Blow) Molding, or Extrusion Blow molding grade, Chemical Resistance and Transparency |
|||
| Flexural Modulus | 2.22 GPa | 322 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics XYLEX X8409AC PC+POLYESTER (Asia Pacific) PC + Polyester, Injection (Blow) Molding, or Extrusion Blow molding grade, Chemical Resistance and Transparency |
|||
| Flexural Modulus | 2.22 GPa | 322 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics XYLEX X8409AC PC+POLYESTER (Europe-Africa-Middle East) PC + Polyester, Injection (Blow) Molding, or Extrusion Blow molding grade, Chemical Resistance and Transparency |
|||
| Flexural Modulus | 2.22 GPa | 322 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP Lexan_BFL2200 PC (Asia Pacific) design for black light frame application as high flow PC, V-2, high reflection grade. |
|||
| Flexural Modulus | 2.22 GPa | 322 ksi | 2.0 mm/min; ISO 178 |
| Styron INSPIREâ„¢ DTF8000 ES Compounded Polypropylene Overview: INSPIREâ„¢ TF 8000 ES is a superior scratch and mar resistant low gloss talc filled interior grad TPO exhibiting excellent low temperature ductility, high modulus and heat performance.M.. |
|||
| Flexural Modulus | 2.22 GPa | 322 ksi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics NORYL GTX GTX942 PPE+PS+PA66 Noryl GTX* GTX942 Resin is a blend of Polyphenylene Ether(PPE) + Polyamide(PA) resin that is designed to have high melt flow for large part/thinwall injection molding. The material is designed to h.. |
|||
| Flexural Modulus | 2.22 GPa | 322 ksi | ASTM D790 |
| Teknor Apex Sinpolene GPP1610 Polypropylene Availability: Africa & Middle East; Latin America; Asia Pacific; South America Additive: Glass Fiber Reinforcement, 10% Filler by Weight Features: Good Dimensional Stability; High Heat Resistance; .. |
|||
| Flexural Modulus | 2.22 GPa | 322 ksi | 2mm/min; ASTM D790 |
| Denka TH-11 Transparent Resin Polymer (MBS resin) Polymethacrylate Butadiene Styrene "TX Polymer" (methyl methacrylate styrene), MS resins as an alternative to acrylic resins, with low density, low moisture absorption, and good moldability, "TH Polymer/TP Polymer," MBS resins with a.. |
|||
| Flexural Modulus | 2.22 GPa | 322 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| SABIC Innovative Plastics Lexan® EXRL0681 PC Copolymer 25 MFR LEXAN High Flow Ductile CopolymerThis data was supplied by SABIC-IP for the Americas region. |
|||
| Flexural Modulus | 2.22 GPa | 322 ksi | ASTM-D790 |
| Polyram RamOfin PPC370B73 Polypropylene, 73% Mineral Filled 73% mineral filled polypropylene for heavy density injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
| Flexural Modulus | 2.22 GPa | 322 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics Lexan® HFD1711 PC Copolymer (Europe-Africa-Middle East) 25 MFR LEXAN High Flow Ductile Copolymer |
|||
| Flexural Modulus | 2.22 GPa | 322 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics Lexan® HFD1731 PC Copolymer (Europe-Africa-Middle East) 25 MFR LEXAN High Flow Ductile Copolymer UV-stabilized |
|||