SABIC Innovative Plastics LNP Thermocomp RX06027 PA 66 (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Bead Filled
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Thermocomp RX06027 PA 66 (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* THERMOCOMP* RX06027 is a compound based on PA 66 containing Glass Bead. Added features include: Easy Molding, Heat Stabilized, UV-Stabilized.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Physical Properties Metric English Comments
Density 1.36 g/cc
0.0491 lb/in³
ISO 1183
Mechanical Properties Metric English Comments
Tensile Strength, Yield 50.0 MPa
7250 psi
5 mm/min; ISO 527
Elongation at Yield 2.5 %
2.5 %
5 mm/min; ISO 527
Tensile Modulus 3.40 GPa
493 ksi
1 mm/min; ISO 527
Flexural Yield Strength 83.0 MPa
12000 psi
2 mm/min; ISO 178
Flexural Modulus 2.90 GPa
421 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 5.00 kJ/m²

@Temperature 23.0 °C
 2.38 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 25.0 kJ/m²

@Temperature 23.0 °C
 11.9 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1U
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 67.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 37.2 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 67.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 37.2 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 61.0 °C
142 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af