SABIC Innovative Plastics LNP Thermocomp OX92080 PPS - LINEAR
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp OX92080 PPS - LINEAR.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* OX92080 is a compound based on Linear PPS containing Proprietary Fillers.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 4.80 g/cc | 4.80 g/cc | ASTM D 792 |
| Density | 4.70 g/cc | 0.170 lb/in³ | ASTM D 792 |
| 4.70 g/cc | 0.170 lb/in³ | ISO 1183 | |
| Moisture Absorption at Equilibrium | 0.00 % @Time 86400 sec |
0.00 % @Time 24.0 hour |
50% RH; ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.0070 cm/cm @Time 86400 sec |
0.0070 in/in @Time 24.0 hour |
ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm @Time 86400 sec |
0.0070 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 58.0 MPa | 8410 psi | 5 mm/min; ISO 527 |
| 60.0 MPa | 8700 psi | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Break | 0.60 % | 0.60 % | Type I, 5 mm/min; ASTM D 638 |
| 0.60 % | 0.60 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 10.84 GPa | 1572 ksi | 1 mm/min; ISO 527 |
| 12.8 GPa | 1860 ksi | 5 mm/min; ASTM D 638 | |
| Flexural Strength | 79.0 MPa | 11500 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 87.0 MPa | 12600 psi | ISO 178 | |
| Flexural Modulus | 11.71 GPa | 1698 ksi | 2 mm/min; ISO 178 |
| 11.9 GPa | 1730 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 0.450 J/cm @Temperature 23.0 °C |
0.843 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 1.23 J/cm @Temperature 23.0 °C |
2.30 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 7.00 kJ/m² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| 4.00 J @Temperature 23.0 °C |
2.95 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 34.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
18.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| CTE, linear, Transverse to Flow | 33.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
18.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 235 °C | 455 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 251 °C @Thickness 3.20 mm |
484 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 162 °C | 324 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 169 °C @Thickness 3.20 mm |
336 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- MV Labs ZN600 ZnI2 Zinc iodide
- SABIC Innovative Plastics Ultem ATX100F PEI+PCE
- Vicone High Performance Rubber VicoSil™ C240Q-RD High Performance Silicone Rubber
- Wanshijie APET Sheet
- Covestro Makrolon® 2407 MAS070 Polycarbonate
- DuPont Teijin Films Melinex® D316 Polyester Film, 200 Gauge
- BASF Styropor® F 215 N Expandable Polystyrene
- Akro-Plastic Akromid® B3 GF 30 RM-M (3016) PA 6 Dry, 30% Glass Filled
- E-Polymers EFLEX® I1010 Ionomer
- Zhejiang Juner PC-A1-7 Top-Grade Flame Retardant UV-Resistant
Copyright © lookpolymers.com All Rights Reserved