SABIC Innovative Plastics LNP STAT-KON DE0069F PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON DE0069F PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-KON* DE0069F is a compound based on Polycarbonate resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant, Superior Molding.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.36 g/cc | 1.36 g/cc | ASTM D792 |
| Density | 1.36 g/cc | 0.0491 lb/in³ | ASTM D792 |
| 1.36 g/cc | 0.0491 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.0700 % | 0.0700 % | 50% RH, 24 hrs; ASTM D570 |
| 0.130 % | 0.130 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.00010 - 0.00030 cm/cm @Time 86400 sec |
0.00010 - 0.00030 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0010 - 0.0040 cm/cm @Time 86400 sec |
0.0010 - 0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 137 MPa | 19900 psi | 5 mm/min; ISO 527 |
| 146 MPa | 21200 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 146 MPa | 21200 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 1.2 % | 1.2 % | 5 mm/min; ISO 527 |
| 1.6 % | 1.6 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 1.2 % | 1.2 % | 5 mm/min; ISO 527 |
| 1.6 % | 1.6 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 16.67 GPa | 2418 ksi | 1 mm/min; ISO 527 |
| 17.32 GPa | 2512 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 212 MPa | 30700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Yield Strength | 210 MPa | 30500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 14.56 GPa | 2112 ksi | 2 mm/min; ISO 178 |
| 14.64 GPa | 2123 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.520 J/cm | 0.974 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.64 J/cm | 8.69 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 24.0 kJ/m² | 11.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 10.0 J @Temperature 23.0 °C |
7.38 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 7.00 µm/m-°C @Temperature -30.0 - 30.0 °C |
3.89 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 7.00 µm/m-°C @Temperature -30.0 - 30.0 °C |
3.89 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 148 °C | 298 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 146 °C @Thickness 3.20 mm |
295 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 143 °C | 289 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 142 °C @Thickness 3.20 mm |
288 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.0 - 4.0 ohm | 1.0 - 4.0 ohm | ASTM D257 |