Polymer Property : Tensile Strength, Yield = 146 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	146 MPa	21200 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP EFL24P PEI LNP* LUBRICOMP* EFL24P is a compound based on Polyetherimide resin containing 20% Glass Fiber, 10% PTFE. Added features of this grade include: Wear Resistant, Exceptional Processing.
Tensile Strength, Yield	146 MPa	21200 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP IFP36 PA6.12 LNP* LUBRICOMP* IFP36 is a Nylon 6/12 base resin containing 30% Glass Fiber, 15% PTFE/Silicone. Added features of t his grade include: Wear Resistant.
Tensile Strength, Yield	146 MPa	21200 psi	ASTM D638
Techmer ES ElectrablendÂ® PC CF20 CR X 20% Carbon Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber Reinforcement, 20% Filler by WeightFeatures: Good Chemical Resistance and Semi ConductiveInformation provided by TP Compos..
Tensile Strength, Yield	146 MPa	21200 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP STAT-KON DE0069F PC LNP* STAT-KON* DE0069F is a compound based on Polycarbonate resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant, Superior Molding.
Tensile Strength, Yield	146 MPa	21200 psi	ASTM D638
Techmer ES HiFillÂ® PA4/6 GF50 ML2 50% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 50% Filler by WeightAdditive: Molybdenum Disulfide LubricantFeatures: LubricatedAppearance: BlackUL File Num..
Tensile Strength, Yield	146 MPa	21200 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP JF008E PES LNP* THERMOCOMP* JF008E is a compound based on Polyethersulfone containing 40% Glass Fiber. Characteristics of this grade are: Easy Molding.
Tensile Strength, Yield	146 MPa	21200 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP STAT-KON OE004AE PPS - Branched LNP STAT-KON* OE004AE is a compound based on PPS - Branched resin containing 20% Carbon Fiber. Added features of this material are: Easy Molding, Electrically Conductive.
Tensile Strength, Yield	146 MPa @Strain 0.200 %, Temperature 871 °C	21200 psi @Strain 0.200 %, Temperature 1600 °F
Carpenter Gall-Tough PLUS™ Stainless, Annealed Data provided by Carpenter Technology Corporation.6.4 mm diameter tensile specimens from center of 25.4 mm diameter bar annealed 1066°C 1 hour, water quenched, and ground.Threshold Galling Stress 4..
Tensile Strength, Yield	146 MPa	21200 psi	ASTM D638
SABIC Innovative Plastics LNP VERTON NV008E PC/ABS (Asia Pacific) LNP* Verton* NV008E is a compound based on PC/ABS resin containing Long Glass Fiber. Added features of this material include: Easy Molding.
Tensile Strength, Yield	146 MPa	21200 psi	ASTM D638
SABIC Innovative Plastics LNP VERTON NV008E PC+ABS LNP* VERTON* NV008E is a compound based on PC+ABS resin containing 40% Long Glass Fiber. Added features of this material include: Easy Molding. Structural.