SABIC Innovative Plastics LNP LUBRICOMP QCP36 PA 6/10 (Asia Pacific)
| Category | Polymer , Thermoplastic , Nylon , Nylon 610 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP QCP36 PA 6/10 (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubricomp* QCP36 is a compound based on Nylon 6/10 resin containing PTFE, Flame Retardant, Carbon Fiber. Added features of this material include: Internally Lubricated, , Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | ASTM D792 |
| 1.32 g/cc | 0.0477 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0035 cm/cm @Time 86400 sec |
0.0035 in/in @Time 24.0 hour |
ISO 294 |
| 0.0040 cm/cm @Time 86400 sec |
0.0040 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm @Time 86400 sec |
0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0080 cm/cm @Time 86400 sec |
0.0080 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 173 MPa | 25100 psi | ASTM D638 |
| 188 MPa | 27300 psi | ISO 527 | |
| Tensile Strength, Yield | 173 MPa | 25100 psi | ASTM D638 |
| 188 MPa | 27300 psi | ISO 527 | |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| 6.2 % | 6.2 % | ISO 527 | |
| Elongation at Yield | 1.9 % | 1.9 % | ISO 527 |
| 2.0 % | 2.0 % | ASTM D638 | |
| Tensile Modulus | 19.2 GPa | 2780 ksi | 1 mm/min; ISO 527 |
| 19.85 GPa | 2879 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 282 MPa | 40900 psi | ASTM D790 |
| 289 MPa | 41900 psi | ISO 178 | |
| Flexural Modulus | 16.54 GPa | 2399 ksi | ASTM D790 |
| 17.0 GPa | 2470 ksi | ISO 178 | |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.01 J/cm | 15.0 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 49.0 kJ/m² | 23.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 6.00 J | 4.43 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.46 | 0.46 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.46 | 0.46 | ASTM D3702 Modified |
| K (wear) Factor | 30.2 x 10-8 mm³/N-M | 15.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 48.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
26.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 48.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
27.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 25.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
14.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 26.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
14.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 222 °C | 432 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 221 °C @Thickness 3.20 mm |
430 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 212 °C | 414 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 212 °C @Thickness 3.20 mm |
414 °F @Thickness 0.126 in |
unannealed; ASTM D648 |